Abstract:Statement of problem: Failure of a fiber post and composite resin core often occurs at the junction between the 2 materials. This failure process requires better characterization. Purpose: The purpose of this study was to evaluate the effect of 2 chemical solvents, hydrogen peroxide and methylene chloride, on the shear bond strength of quartz and glass fiber posts to a composite resin. Material and methods: Twenty-four posts (3 +/-0.1 mm in length) were prepared for each quartz (LIGHT-POST (LP)) and glass fiber (Cytec blanco (CB)) post. Posts were horizontally embedded in acrylic resin with half of the post diameter exposed. The exposed surfaces were successively ground with 400-, 800-, and 1200-grit silicon carbide papers, to ensure uniform smoothness. The specimens were divided into 3 subgroups (n=8) representing different surface treatment techniques, including application of silane for 60 seconds (S), etching with hydrogen peroxide for 20 minutes (H), and etching with methylene chloride for 5 seconds (M). Silane-treated specimens served as controls. A dual-polymerized composite resin (Tetric EvoCeram) was placed in a polytetrafluoroethylene mold (30 x 2 mm) positioned upon the post specimens and polymerized for 20 seconds with a light-emitting diode (LED) polymerization unit. The specimens were stored in water at 37 degrees C for 24 hours. Shear bond strength values (MPa) of posts and composite resin cores were measured using a universal testing machine with a crosshead speed of 0.5 mm/min. Data were analyzed by 2-way analysis of variance (ANOVA). Post hoc Tukey intervals for comparison among the 2 post materials and 3 surface treatment techniques were calculated (alpha =.05). The effect of the chemical surface treatments on glass and quartz fiber post surfaces were examined with a scanning electron microscope (SEM). Results: There were significant differences between the shear bond strength for LP and CB (P<.001). For all groups, the application of H showed the highest bond strength values. There was no significant difference between the S and M groups (P>.05). The SEM observations demonstrated that the fiber post surfaces were modified after chemical surface treatment techniques. Conclusions: The surface treatment of quartz and glass fiber posts with hydrogen peroxide significantly enhanced the shear bond strength of the composite resin tested due to its ability to dissolve the epoxy resin matrix used in each post. The lowest bond strength was obtained with M and S groups. Application of methylene chloride to the fiber post surfaces for 5 seconds was not effective in increasing the shear bond strength of the fiber post to composite resin.

Fabrication and Measurement of Mechanical Properties of a Radiopaque Quartz Fiber Post

Development of dental posts by carbon fiber reinforced resin

Study on the Mechanical Properties of Quartz Fiber-Reinforced Composite for Canal Post

Clinical application of new type of carbon fiber reinforced resin post

Multifunctional Epoxy Resin-Based Composites with Excellent Flexural Strength and X-ray Imaging Capacity Using Micro/nano Structured QF-Bi2SiO5 Fillers.

Flexural modulus, flexural strength, and stiffness of fiber-reinforced posts

Mechanical properties of basalt fiber-reinforced denture base resin

Flexural Strength of Dental Fiber Composite Post Manufactured with a Novel Approach

Effects of chemical surface treatments of quartz and glass fiber posts on the retention of a composite resin

Surface modifications of short quartz fibers and their influence on the physicochemical properties and in vitro cell viability of dental composites

The bond strength between fiber posts modified with barium sulfate and resin core materials

The Physiochemical Properties of Dental Resin Composites Reinforced with Milled E-glass Fibers

Fabrication and Characterization of Dental Restorative Composites with Gradient Properties

Formulation and Characterization of New Experimental Dental Composites with Zirconium Filling in Different Forms

Study on the microtensile bond strength of fiber post and resin core using different surface treatments technology

The effects of different chemical etching agents on the surface morphology and flexural strength of fiber posts

Fabrication by stereolithography of fiber-reinforced fused silica composites with reduced crack and improved mechanical properties

The researchment of nami-material reinfoced dental composite resin

Investigation of Material Properties of One-Piece Glass Fiber Post-and-Core Affecting Biomechanical Responses of the Restorative System

Progress of Research on Fiber Posts

Dental fiber-post resin base material: a review.