Abstract:Statement of problem: Failure of a fiber post and composite resin core often occurs at the junction between the 2 materials. This failure process requires better characterization. Purpose: The purpose of this study was to evaluate the effect of 2 chemical solvents, hydrogen peroxide and methylene chloride, on the shear bond strength of quartz and glass fiber posts to a composite resin. Material and methods: Twenty-four posts (3 +/-0.1 mm in length) were prepared for each quartz (LIGHT-POST (LP)) and glass fiber (Cytec blanco (CB)) post. Posts were horizontally embedded in acrylic resin with half of the post diameter exposed. The exposed surfaces were successively ground with 400-, 800-, and 1200-grit silicon carbide papers, to ensure uniform smoothness. The specimens were divided into 3 subgroups (n=8) representing different surface treatment techniques, including application of silane for 60 seconds (S), etching with hydrogen peroxide for 20 minutes (H), and etching with methylene chloride for 5 seconds (M). Silane-treated specimens served as controls. A dual-polymerized composite resin (Tetric EvoCeram) was placed in a polytetrafluoroethylene mold (30 x 2 mm) positioned upon the post specimens and polymerized for 20 seconds with a light-emitting diode (LED) polymerization unit. The specimens were stored in water at 37 degrees C for 24 hours. Shear bond strength values (MPa) of posts and composite resin cores were measured using a universal testing machine with a crosshead speed of 0.5 mm/min. Data were analyzed by 2-way analysis of variance (ANOVA). Post hoc Tukey intervals for comparison among the 2 post materials and 3 surface treatment techniques were calculated (alpha =.05). The effect of the chemical surface treatments on glass and quartz fiber post surfaces were examined with a scanning electron microscope (SEM). Results: There were significant differences between the shear bond strength for LP and CB (P<.001). For all groups, the application of H showed the highest bond strength values. There was no significant difference between the S and M groups (P>.05). The SEM observations demonstrated that the fiber post surfaces were modified after chemical surface treatment techniques. Conclusions: The surface treatment of quartz and glass fiber posts with hydrogen peroxide significantly enhanced the shear bond strength of the composite resin tested due to its ability to dissolve the epoxy resin matrix used in each post. The lowest bond strength was obtained with M and S groups. Application of methylene chloride to the fiber post surfaces for 5 seconds was not effective in increasing the shear bond strength of the fiber post to composite resin.

The effects of different chemical etching agents on the surface morphology and flexural strength of fiber posts

Influence of luting agents on fracture resistance of endodontically treated incisors with metal posts

Development of dental posts by carbon fiber reinforced resin

Effects of chemical surface treatments of quartz and glass fiber posts on the retention of a composite resin

Study on the microtensile bond strength of fiber post and resin core using different surface treatments technology

Effect of Crosslinked Chitosan Nanoparticles on the Bonding Quality of Fiber Posts in Root Canals.

Surface treatment of glass fiber and carbon fiber posts: SEM characterization

Effect of Etching Time and Resin Bond on the Flexural Strength of IPS E.max Press Glass Ceramic.

The influence of autoclave sterilization on elastic module and flexural strength of five types of posts

[H(2)O(2) Treatment Improves the Bond Strength Between Glass Fiber Posts and Resin Cement].

Influence of Proanthocyanidins Combined with Ethanol-Wet Bonding on the Bonding Quality of Fibre Posts to Root Dentine.

Effect of surface treatments on fracture resistance of root filled teeth with bonded fibre posts

Flexural modulus, flexural strength, and stiffness of fiber-reinforced posts

Effects of pretreatment in post space on the bonding strength of self-adhesive resin cement to fiber posts

[Effect of Hydrofluoric Acid Etching Time and Resin Bonding on the Flexural Strength of Lithium Disilicate Glass Ceramic].

Effect of Posts Surface Treatments on the Pull-out Bond Strength of Glass Fiber Post to Root Dentin “A Comparative In-Vitro Study”

Effect of Post-Space Treatment on Retention of Fiber Posts in Different Root Regions Using Two Self-Etching Systems.

Final Irrigant Temoporfin, Femtosecond Laser, and Chitosan Nanoparticles on Extrusion Bond Strength of Glass Fiber Post, Microhardness, and Modulus of Elasticity of Canal Dentin

Effect on the bond strengths of glass fiber posts functionalized with polydopamine after etching with hydrogen peroxide.

Bending properties of glass fiber-reinforced plastic for post materials evaluated by cantilever test

Flexural Strength of Dental Fiber Composite Post Manufactured with a Novel Approach