Effect of Etching Time and Resin Bond on the Flexural Strength of IPS E.max Press Glass Ceramic.

Luo Xiaoping,Ren Dongfeng,Nick Silikas

DOI: https://doi.org/10.1016/j.dental.2014.08.373

IF: 5.687

2014-01-01

Dental Materials

Abstract:Objectives. To evaluate the effect of hydrofluoric acid (HFA) etching time and resin cement bond on the flexural strength of IPS e.max (R) Press glass ceramic.Methods. Two hundred and ten bars, 25 mm x 3 mm x 2 mm, were made from IPS e.max (R) Press ingots through lost-wax, hot-pressed ceramic fabrication technology and randomly divided into five groups with forty-two per group after polishing. The ceramic surfaces of different groups were etched by 9.5% hydrofluoric acid gel for 0, 20, 40, 60 and 120 s respectively. Two specimens of each group were selected randomly to examine the surface roughness and 3-dimensional topography with atomic force microscope (AFM), and microstructure was analyzed by the field emission scanning electron microscope (FE-SEM). Then each group were subdivided into two subgroups (n = 20). One subgroup of this material was selected to receive a thin (approximately 0.1 mm) layer of resin luting agent (Variolink N) whereas the other subgroup remained unaltered. Half of subgroup's specimens were thermocycled 10,000 times before a 3-point bending test in order to determine the flexural strength. Interface between resin cement and ceramic was examined with field emission scanning electronic microscope.Results. Roughness values increased with increasing etching time. The mean flexural strength values of group 0 s, 20 s, 40 s, 60 s and 120 s were 384 +/- 33, 347 +/- 43, 330 +/- 53,327 +/- 67 and 317 +/- 41 MPa respectively. Increasing HF etching times reduced the mean flexural strength (p < 0.05). However, the mean flexural strength of each group, except group 0 s, increased significantly to 420 +/- 31, 435 +/- 50, 400 +/- 39 and 412 +/- 58 MPa after the application of dual-curing resin cement. In the present investigation, no significant differences after thermocycling on the flexural strengths were evident.Significance. Overtime HF etching could have a wakening effect on IPS e.max (R) Press glass ceramic, but resin cement bonding to appropriately etched surface would strengthen the dental ceramic. (C) 2014 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.