Influence of luting agents on fracture resistance of endodontically treated incisors with metal posts

Xinhua GU,Caiyun MAO,Xiaoxiang WANG

DOI: https://doi.org/10.3969/j.issn.1003-7632.2007.06.024

2007-01-01

Abstract:Objective This study was to evaluate whether resin luting system could improve the fracture resistance of endodontically treated incisors with prefabricated and cast metal posts.Methods Fourty intact maxillary central incisors after endodontical treatments were randomly assigned to four groups of 10 teeth each. The teeth were then restored with prefabricated titanium alloy posts or cast nickel-chromium post-and-cores and metal-ceramic crowns. The posts and crowns were cemented with either adhesive composite resin luting system or glass ionomer cement. All restored teeth were thermocycled for 5000 cycles (5℃/55℃) as a fatigue test. Each specimen was secured in a universal testing machine. A compressive load was applied at an angle of 135 degrees to the long-axis of the tooth with a crosshead speed of 1.5mm/s until initial fracture. Fracture loads and modes (repairable or catastrophic) were recorded.Results The fracture load was 499.82±168.90N in the group of Ti-alloy post with resin cement (group 1) and was 388.98±125.22N in the group of the same posts with glass ionomer cement (group 2); The fracture load in the group of cast post with resin cement (group 3) was 412.55±99.29N,while 337.41±121.18N in the group of the same posts with glass ionomer cement (group 4). The repairable fracture observed from Group 1 to Group 4 was 40%, 20%, 20% and 30% respectively. No significant difference was found for fracture load and fracture mode between groups with different luting agents (P>0.05).Conclusion It indicates that adhesive composite resin luting system might not significantly improve the fracture resistance of the pulpless incisors restored with metal posts.