Shear Bond Strength to Enamel, Mechanical Properties and Cellular Studies of Fiber-Reinforced Composites Modified by Depositing SiO2 Nanofilms on Quartz Fibers via Atomic Layer Deposition
Fei Shu,Hong Chen,Zhihao Zhang,Zhiyue Dun,Weijin Lv,Wangxinyue Sun,Mei Liu
DOI: https://doi.org/10.2147/ijn.s446584
IF: 7.033
2024-03-06
International Journal of Nanomedicine
Abstract:Fei Shu, &ast Hong Chen, &ast Zhihao Zhang, Zhiyue Dun, Weijin Lv, Wangxinyue Sun, Mei Liu Department of Prosthodontics, The Affiliated Stomatological Hospital of Nanjing Medical University, Jiangsu Province Key Laboratory of Oral Diseases, Jiangsu Province Engineering Research Center of Stomatological Translational Medicine, Nanjing, People's Republic of China &astThese authors contributed equally to this work Correspondence: Mei Liu, Department of Prosthodontics, The Affiliated Stomatological Hospital of Nanjing Medical University, Jiangsu Province Key Laboratory of Oral Diseases, Jiangsu Province Engineering Research Center of Stomatological Translational Medicine, Nanjing, People's Republic of China, Tel +86-25-69593081, Fax +86-25-69593186, Email Introduction: Poor interfacial bonding between the fibers and resin matrix in fiber-reinforced composites (FRCs) is a significant drawback of the composites. To enhance the mechanical properties of FRC, fibers were modified by depositing SiO 2 nanofilms via the atomic layer deposition (ALD) technique. This study aims to evaluate the effect of ALD treatment of the fibers on the mechanical properties of the FRCs. Methods: The quartz fibers were modified by depositing different cycles (50, 100, 200, and 400) of SiO 2 nanofilms via the ALD technique and FRCs were proposed from the modified fibers. The morphologies, surface characterizations of nanofilms, mechanical properties, and cytocompatibility of FRCs were systematically investigated. Moreover, the shear bond strength (SBS) of FRCs to human enamel was also evaluated. Results: The SEM and SE results showed that the ALD-deposited SiO 2 nanofilms have good conformality and homogeneity. According to the results of FTIR and TGA, SiO 2 nanofilms and quartz fiber surfaces had good chemical combinations. Three-point bending tests with FRCs showed that the deposited SiO 2 nanofilms effectively improved FRCs' strength and Group D underwent 100 deposition cycles and had the highest flexural strength before and after aging. Furthermore, the strength of the FRCs demonstrated a crescendo-decrescendo tendency with SiO 2 nanofilm thickness increasing. The SBS results also showed that Group D had outstanding performance. Moreover, the results of cytotoxicity experiments such as cck8, LDH and Elisa, etc., showed that the FRCs have good cytocompatibility. Conclusion: Changing the number of ALD reaction cycles affects the mechanical properties of FRCs, which may be related to the stress relaxation and fracture between SiO 2 nanofilm layers and the built-up internal stresses in the nanofilms. Eventually, the SiO 2 nanofilms could enhance the FRCs' mechanical properties and performance to enamel by improving the interfacial bonding strength, and have good cytocompatibility. Keywords: atomic layer deposition, SiO 2 nanofilms, surface modification, interfacial bonding Graphical Fiber-reinforced composite (FRC) is the most popular clinically used dental restorative material. 1,2 It is commonly used for post-implant transitional restorations (crowns and bridges) and traumatic tooth fixation, as it meets patient functional and aesthetic requirements for dental restorations; moreover, it has the advantages of short chairside operation time, good patient experience, and less foreign body sensation. 3 However, the rate of postoperative failure in clinical follow-up research remains considerably high. 4,5 Ahmeda showed a Kaplan–Meier survival probability of 94.5% for FRC fixed partial denture, follow up periods ranged between 2 months and 8 years. FRC fracture and dislodgement occurred significantly more than other types of failures. 6 Stress concentration occurs at the enamel/FRC interface. The stress transmitted to the FRC can be relieved by initiation of a crack and its propagation through the FRC, eventually leading to detachment and fracture. 7 Tacken et al showed that when the FRC was used as an orthodontic retainer, FRC dislodgement and fracture remained the most common failure factors, accounting for 70% of all failures, after 24 months of follow-up. 8 Therefore, it is crucial to enhance mechanical properties for improving the intraoral long-term service performance of FRC. As an organic/inorganic composite, the strength of the FRC depends not only on the strength of the fiber and resin complex but also on the strength of the interfacial bond between them. When the complex undergoes stress, a strong interface bond can effectively disperse stress and prevent crack propagation at the interface. The first structure to break down is the weakly -Abstract Truncated-
pharmacology & pharmacy,nanoscience & nanotechnology