Abstract:By adjusting the KOH/H2O texturing condition intendedly, different random pyramidal textures with the average pyramid size of 8 μm (large), 4 μm (medium) and 1.5 μm (small) were prepared on N type M2 monocrystalline silicon substrates for the fabrication of silicon heterojunction (SHJ) solar cell. It was evidenced that the pyramid morphology not only impacted the reflection of incident light and the heterojunction interface passivation quality but also affected the interface contact property between transparent conductive oxide (TCO) layer and Ag electrode. The texture with small pyramids presented the best anti-reflective and passivation performance due to the pyramidal size distribution uniformity, which brought the SHJ solar cell the highest short-circuit current density (JSC) and open-circuit voltage (VOC). However, the texture with small pyramids also led to the worst fill factor (FF). As a result, there was no obvious difference on the conversion efficiency for the textures with different pyramidal size. By characterizing the TCO/Ag contact, the FF reduction induced by the small pyramid texture could be attributed to the increased specific contact resistance of the TCO/Ag contact, which resulted from the fact that there were lots of voids between the TCO layer and Ag electrode, since Ag particles with a larger size than the small pyramids could not fill into the limited space between the adjacent pyramids. As a result, in order to realize the potential to enhance the SHJ solar cell conversion efficiency by adopting the texture with small pyramids, new Ag paste with smaller Ag particles should be adopted.

Small Pyramids Texture and Performance of Mono-crystalline Silicon Solar Cells

A Simple Texturization Approach for Mono-Crystalline Silicon Solar Cell with Low Tmah Concentration Solution

INFLUENCE OF SUB-SURFACE DAMAGE ON TEXTURING OF MONOCRYSTALLINE SILICON WAFERS FOR SOLAR CELLS

Texturization of Mono-Crystalline Silicon Solar Cells in TMAH Without the Addition of Surfactant

Pyramid size control and morphology treatment for high-efficiency silicon heterojunction solar cells

TEXTURIZATION OF MONOCRYSTALLINE SILICON FOR SOLAR CELLS

Constructing Submicron Textures on Mc-Si Solar Cells Via Copper-Catalyzed Chemical Etching

Influence of the textured pyramid size on the performance of silicon heterojunction solar cell

Formation of Various Pyramidal Structures on Monocrystalline Silicon Surface and Their Influence on the Solar Cells

Ultrafast Random‐Pyramid Texturing for Efficient Monocrystalline Silicon Solar Cells

New Surface Microstructure of Mono-Si Wafer Textured Using Wet Chemical Solutions for Solar Cell (revised Paper (2))

Investigations Of Random Pyramid Texture On The Surface Of Single-Crystalline Silicon For Solar Cells

Nano-Texturing of Single Crystalline Silicon Via Cu-Catalyzed Chemical Etching

Investigation of Texturization for Monocrystalline Silicon Solar Cells with Different Kinds of Alkaline

The Influence of New Additive in Alkaline Solution on the Shape of Pyramid on the Monocrystal Si Surface

Texturization of Cast Multicrystalline Silicon for Solar Cells

Enhanced Efficiency of Graphene-Silicon Schottky Junction Solar Cell through Pyramid Arrays Texturation

Improvement of conversion efficiency of multicrystalline silicon solar cells by incorporating reactive ion etching texturing

Acid Texturing of Large Area Multi-Crystalline Silicon Wafers for Solar Cell Fabrication

Reflectivity of porous-pyramids structured silicon surface

Investigation of Texturing Industrial Mono-Crystalline Silicon Solar Cells