Hydrothermal Synthesis Of Acicular Lead Titanate Fine Powders
Humin Cheng,Jiming Ma,Zhenguo Zhao,Di Qiang,Yongxiang Li,Xi Yao
DOI: https://doi.org/10.1111/j.1151-2916.1992.tb05548.x
IF: 4.186
1992-01-01
Journal of the American Ceramic Society
Abstract:A pure, acicular lead titanate (PbTiO3) fine powder with a white color has been prepared by hydrothermal synthesis. It is a new phase of PbTiO3, with I4 symmetry, cell parameters of a = 12.358 angstrom and b = 14.541 angstrom, and a density of 6.80 g . cm-3. The influences of pH (12.5 to 14.4), Pb/Ti ratio (1.0 to 1.6) in the feedstock, reaction temperature (130-degrees to 230-degrees-C), time (0.25 to 4 h), starting materials, and additives on the formation of acicular PbTiO3 under hydrothermal conditions have been investigated. The acicular PbTiO3 with I4 symmetry, referred to as the PX phase, can be converted to the perovskite-type (PE phase) of PbTiO3 at about 605-degrees-C while its acicular morphology is essentially unchanged. The preferable conditions for preparing pure acicular PX-phase PbTiO3 are that the pH is 13.0 to 14.0, Pb/Ti ratio is > 1.3, reaction temperature is 170-degrees to 200-degrees-C, time is 0.5 to 1.0 h, titanium butoxide (Ti[O(CH2)3CH3]4) is the starting material, and poly(vinyl alcohol) is an additive. The acicular grain of the PX phase is usually less than 100 nm in diameter and more than 1000 nm in length.