Tracking Supervision of Service Performance and Life Assessment of Defective 15Cr1Mo1V Steel Pipeline
Xian Xi Xia,Bao Yin Zhu,Guo Dong Zhang,Jin Hua Shi
DOI: https://doi.org/10.4028/www.scientific.net/KEM.795.318
2019-10-07
Key Engineering Materials
Abstract:A large number of inclusion defects were found during the metal supervision process of 15Cr1Mo1V steel main steam pipeline of the Russian-made thermal power unit. In this paper, the tracking supervision research of 15Cr1Mo1V steel pipe elbow with inclusion defects is carried out. The variation law of strength, toughness, metallographic structure and creep rupture strength with inclusion defects at different operating time is studied. Type and composition of inclusions are analysed and creep fatigue crack evaluation of the most serious inclusion defects discovered is performed. The results show that with the increase of service time, the room temperature and high temperature strength of the material gradually decreased, the impact toughness deteriorated, the ductile-brittle transition temperature increased and greater than room temperature, the metallurgical organization aging grade rose from 3 to 4, creep rupture strength decreased, creep aging was increasingly serious, and creep residual life reduced. The main inclusions are plastic MnS、SiO 2 and severe inclusion levels up to 3. Longitudinal inclusions are mostly long-chain features, and the ends are sharp but no sharp cracks are found at the sharp ends; the transverse inclusions are granular. Creep fatigue crack evaluation show that there was no obvious growth of material inclusion defects with the increase of service time, it is necessary to strengthen the supervision and inspection of brittle inclusions in the follow-up operation. Periodical: Main Theme: Edited by: Jian Ming Gong, Ming-Liang Zhu and Shan Tung Tu Pages: 318-324 DOI: https://doi.org/10.4028/www.scientific.net/KEM.795.318 Citation: X. X. Xia et al., "Tracking Supervision of Service Performance and Life Assessment of Defective 15Cr1Mo1V Steel Pipeline", Key Engineering Materials, Vol. 795, pp. 318-324, 2019 Online since: March 2019 Authors: Keywords: Export: Price: 36,00 € Permissions: Request Permissions Share: * - Corresponding Author [1] Cheng Jianguo, Yu Lichen, Song Jianhua, et al. Study on the variable amplitude thermal fatigue crack growth life of high temperature and high pressure steam branch pipelines. Chemical Industry and Engineering, 1996, 23(5): 289-293. [2] M Zrilic, Z Burzic, Z Cvijovic. Fracture Toughness and Crack Resistance of Steam Pipeline Steel in Initial and Used States. Strength of Materials, 2004, V 36(1): 47-58. DOI: https://doi.org/10.1023/b:stom.0000020114.57953.e9 [3] Wen Wei. Method for assessing the life of fixed steam and hot water boilers and steam and hot water pipes elbows. Boiler Technology, 1993, (10): 22-32. [4] W Suna, T H Hydea, A A Beckera, et al. Some key effects on the failure assessment of weld repairs in CrMoV pipelines using continuum damage modeling. Engineering Failure Analysis, 2005, 12(5): 720-745. DOI: https://doi.org/10.1016/j.engfailanal.2004.12.006 [5] Shu Guogang, Li Yimin, Zhao Yanfen et al. Life extrapolation calculation method of 12CrlMoV steel based on creep curve. Thermal Power Generation, 2000(6): 32-35. [6] Dolzhanskii P R. Peculiarities of assessing the remaining service life of steam pipelines for operation beyond the fleet resource. International Journal of Pressure Vessels and Piping, 2005, 82(7): 546-552. [7] Xiong Xianren. Damage Evolution and Life Estimation Method of High Temperature Steam Pipeline under Interaction of High Temperature Creep and Low Cycle Fatigue. Jiangxi Science, 2005, 23(1): 9-13. [8] -Abstract Truncated-