Abstract:A series of mixed MgAl-HTlc, Mg1-xAlx-NO3-HTlc (where X=M(III)/(M(III)+ M(II))=1/3 in the starting solution) were prepared following the coprecipitation method at a constant pH under different synthesis temperatures. Their structural, textual and rheological properties were examined respectively. It is found from the results that the increase of the synthesis temperature will increase the interlayer spacing of the layered compounds, but under the room temperature, the sample shows the best crystallinity. Nitrogen adsorption isotherms were used to determine the surface areas and pore structure of these compounds, and the effect of the synthesis temperature on the surface characteristics is discussed. It is thought that the microporosity was related to the treatment temperature, and most of the samples contain large amount of micropores about 1.5 nm. The results of the hydrated diameters showed that all the samples are polydispersity, but flocculation occurred in the samples, which were prepared under higher temperatures. The flow curve of the suspension showed that the samples, which were prepared under relatively low temperatures, behaved as Newton-like behavior with a slight shear-thickening, whereas the flow curves of the other samples, which were prepared under higher temperatures, are shear-thinning, typical behavior of the flocculated system. The result of the rheology is accordant with the results of the hydrated diameters, the coagulation suspension showed the non-Newton flow behavior, whereas the other suspensions showed the Newton-like flow.

Synthesis and Characterization of Intercalation Assembled Supermolecular Structure Anion Pillared Hydrotalcites

Pillared hydrotalcite produced by calcine-recovering method and its structure characterization.

Synthesis and Thermal Stability of Oxalate-intercalated Hydrotalcites

Novel Intercalation Metal Complexes: Microwave Synthesis, Crystal Structure and Properties

Pillaring and Polymerization of Vinylbenzene Sulfonate in the Interlayer of Hydrotalcite

Studies on Synthesis, Characterization and Catalytic Behavior of Hydrotalcite Pillared with Peroxoheteropolyanions

Synthesis and Characterization of the Mixed Mg/Al Hydrotalcite‐Like Compounds

Synthesis, Characterization and Growth Mechanism of Hierarchical Cantaloupe-Like Alooh Superstructures by A Simple Hydrothermal Process

THE SYNTHESIS AND CHARACTERIZATION OF CARBONATE PILLARED Co-Al HYDROTALCITE-LIKE COMPOUND

Sulfanilic-pillared LDHs Prepared by Different Methods

Preparation and Characterization of Cetyl Trimethylammonium Intercalated Sericite

ChemInform Abstract: Synthesis of Calcium Alanate and Its Dehydriding Performance Enhanced by FeF3 Doping.

One-Step Synthesis of Hierarchical Cantaloupe-Like Alooh Superstructures Via A Hydrothermal Route

Synthesis and characterization of tetrathiotungstate intercalated NiAl layered double hydroxides: Effects of synthesis conditions

Preparation, Pillarinc Structure and Thermal Stability of Hydroxy-Fe-Al Pillared Clays Containing Mixed-Metal Complexes (I)

Stability of hydrotalcite (Mg-Al layered double hydroxide) in presence of different anions

Adipate-Intercalated LDHs Prepared by Different Methods

Syntheses and Characterization of Silica - Pillared Layered Ferrititanates

Designed formation of the stable adduct InP/CTAB/Clay

Directly Systhesis of Layered Double Hydroxides Pillaring with Organic Anions by Homogeneous Precipitation

Theoretical Studies On Layer Composition, Structure And Properties Of Hydrotalcite