PREPARATION AND CHARACTERIZATION OF HYDROXY-FeA 1 PILLARED CLAYS
DONGYUAN ZHAO,GUOJIA WANG,YASHU YANG,XIEXIAN GUO,QIBIN WANG,JIYAO REN
2006-01-01
Abstract:-Solutions containing hydroxy-FeA1 oligocations (HFA) were prepared by two procedures: (1) treatment of a mixture of FeC13 and A1C13 with aqueous Na2CO3, followed by aging of the product and (2) preliminary preparation and aging of hydroxy-Al~3 oligocations followed by reaction of the latter with aqueous FeC13. Ion-exchange of Na-montmorillonite with HFA yield pillared clay (designated as FeA1PILC) with d(001) values of 1.98-1.56 nm and a surface area of 230 mVg. The pillar structure, thermal stability, surface acidity, and reduction behavior of the pillared clays were determined by 27A1-NMR, XRD, DTA, M6ssbauer spectroscopy, Py-IR, TPD, TPR. Fe/A1 ratios greatly affect the pillar structure, surface area and thermal stability of FeA1-PILC. The pillar in FeAI-PILC with Fe/A1 ratio <0.5 has a Keggin structure, similar to that of AI-PILC, but the pillar structures of FeA1-PILC with Fe/A1 >-0.5 are the ferric tripolymer species similar to those of Fe-PILC. The basal spacings, surface area, and thermal stability are decreased with increasing Fe/A1 ratio. There is relatively strong interaction between Fe and A1 in the pillars. The interaction is enhanced with decreasing Fe/A1 ratio. Reduction of the Fe phase in FeA1-PILC was reduced by the interaction of Fe with A1. Key Words--Acidity, Hydroxy-FeA1 pillars, Pillared clay, Preparation, Stability. I N T R O D U C T I O N Naturally occurring montmoril lonite clays are layered alumino-silicates which, in their natural state, are held together by weak electrostatic forces. New classes of materials have recently been developed by exchanging the small Na + ions that are normally found between these layers with inorganic metal ions of larger size and charge (Brindley and Semples, 1977; Lahav et al., 1978; Vaughan, 1979). The N2 BET surface areas of these "pillared clays" increase typically from ca. 20 mZ/g before pillaring to greater than 230 m2/g. Inorganic polymeric metal ions derived from watersoluble salts of AI, Fe, Cr, Bi, Mg, Zr, Co, and Ni appear to be the most widely explored pillaring agents (Leoppert et al., 1979) although it has been reported that Mo, Nb, Si, and other metal ions have been successful (Endo et al., 1980, 1981; Shabtai, 1980). A related study recently disclosed a class of hydroprocessing catalysts reported (Shabtai and Fijal, 1986) to be comprised of, for example, a Ni +2 or Co +2 ionexchanged smectite that is then cross-linked with hydroxy-A1 oligomers. This material is calcinated at 400500~ and treated with an ammon ium molybdate solution to yield the hydroprocessing catalyst. In view of the above studies it was of interest to J To whom correspondence should be addressed. Present address: Department of Fine Chemical Technology, Shenyang Institute of Chemical Technology, Shenyang 110021, P. R. China. Copyright 9 1993, The Clay Minerals Society synthesize well-defined hydroxy-FeAl oligocations for use as pillaring agents. In this paper, a series of hydroxy-FeAl pillared clays (FeA1-PILC) with various Fe/A1 ratios were prepared by two methods. The thermal stability, reduction behavior, structural properties, and surface acidity of the mixed pillared clays were determined by XRD, DTA, IR, TPR, TPD, and Mrssbauer spectroscopy. EXPERIMENTAL MATERIALS AND METHODS