Effect of Biybo3 Solid Solution Limit on Electric Properties and Structure of Bspt Piezoceramics

Shi Wei,Leng Sen-Lin,Long Yu,Zhu Jian-Guo,Xiao Ding-Quan

DOI: https://doi.org/10.3724/sp.j.1077.2013.12476

IF: 1.292

2013-01-01

Journal of Inorganic Materials

Abstract:yBiYbO(3)-(0.36-y)BiScO3-xPbTiO(3) (BSYPT-0.64/y) piezoelectric ceramics were prepared by traditional solid reaction method. The result of X-ray diffraction shows that the as-prepared BSYPT-0.64/y ceramics have single perovskite structure. However, scanning electron microscopy results show that the surface morphology of BSYPT-0.64/y ceramics becomes abnormal at y=0.1, and a large amount of tiny grains, with the grain size distributing from 0.3 mu m to 0.5 mu m, separate out on the surface of the ceramics at y=0.14. EDS analysis reveals that the major ingredients of these tiny grains are mainly Bi, Yb, Ti, Sc and O. The solid solution limit is therefore confirmed to be near y=0.1 for the BSYPT-0.64/y ceramics. By means of systematic piezoelectric, ferroelectric and temperature-dependent dielectric (T-c similar to 450 degrees C) characterizations, it is found that the occurrence of solid solubility limit-related BiYbO3 separation is not a key factor for affecting the electrical properties and structure of the ceramics, but a relatively isolated behavior. The degradation of structural and electrical properties is attributed to the decrease in Sc/Pb ratio when the BiYbO3 content is increased, which leads to a deviation from MPB in the BSYPT-0.64/y ceramics.