High-press preparation and thermoelectric properties of Bi0.90Sb0.10

Chunmei Song,HuaJun Liu,YunLong Wu,XiaoDong Jiao,Rongjin Huang,Hong Wang,LaiFeng Li
DOI: https://doi.org/10.3969/j.issn.1000-6516.2005.06.005
2005-01-01
Abstract:Nano crystallite Bi_(0.90)Sb_(0.10) powders were prepared by mechanical alloying.The powders were pressed into pellets and then pressed to form bulk samples under high pressure of 6 GPa at different pressing temperatures(373 K,473 K and 573 K).The X-ray diffraction analysis indicated that the single phase was formed.Electrical conductivity,Seebeck coefficient and thermal conductivity were all measured at the temperature range of 80 K-300 K.The electrical conductivity and thermal conductivity were lower than that of single crystal because of boundary scattering.The Seebeck coefficients had a maximum value 120.3 μV/K at about 130 K.The largest figure-of-merit was 0.90×10~(-3) K~(-1) at 140 K.