Abstract:A new type of coagulant, polysilicate-ferric-zinc (PSFZn) with different Fe/Zn molar ratios, was synthesised using water glass (industrial grade, w(SiO2) = 21 mass %, ρ = 1.34 × 103 kg m−3, modulus = 3.2), FeSO4 · 7H2O, ZnSO4, and NaClO3 by way of co-polymerisation in the same (Fe + Zn)/Si molar ratio based on polysilicate-ferric (PSF). The effect of the Fe/Zn molar ratios on the morphology and structure was systematically investigated using scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), and X-ray diffraction (XRD) analysis. Three samples, namely PSFZn4, PSFZn1, and PSFZn0.25, represented Fe/Zn molar ratios of 4, 1, and 0.25, respectively, and were selected for a comparative study while a constant (Fe + Zn)/Si molar ratio equal to 1 was maintained. Accordingly, PSFZn was found to be a complex compound rather than a simple mixture of raw materials. With the decrease in Fe/Zn, a great change occurred in the surface morphology, from a tetrahedral cluster structure to a lamellar structure. The Fe—O and Fe—O—Si bonds were gradually replaced by Zn—O and Zn—O—Si. However, the crystalline peaks were more obvious with the increase in the number of zinc ions; hence the new polymer would be formed from iron, zinc, and polysilicate. In addition, the coagulation performance of PSFZn was investigated using a surface water sample. PSFZn4 exhibited a better coagulation performance than the other PSFZn coagulants. Additionally, the trends in changes in pH with different coagulation times after adding PSFZn were studied relative to PSF and FS. The replacement of zinc ions with iron ions could effectively counter the rapid decrease in pH. The effect of settling time on the coagulation efficiency was also investigated. PSFZn4 exhibited a better settlement performance than PSF and poly aluminium chloride (PAC). Hence, the partial substitution of zinc salt with iron salt not only addresses the inadequacies of iron salt but also improves the coagulation efficiency of zinc salt in water treatment.

STUDY ON THE PREPARATION AND FLOCCULATION PERFORMANCE OF POLY-ZINC SILICATE

Preparation and Performance Analysis of Inorganic Polymer Flocculant PZFSiC

Preparation of Polyferric Silicate Sulfate Flocculant and Its Flocculation Properties

Preparation and Application of Slag Compound Flocculant

Study on Preparation and Flocculation Properties of Inorganic Polymer Flocculant Polyferric Silicate Sulfate (Pfss)

Research on the preparation of composite polysilicic acid flocculants and their performances

Study on the Performance of a Novel Inorganic Polymeric Flocculant

Study on the preparation of polysilicate ferric flocculant and its treatment of high turbidity tailings water

Study on Preparation of Polysilicate Chloride Aluminum and Ferric Flocculant with Fly Ash

A New Efficient Flocculant-Preparation and Property of Poly (silicon/aluminum/ferric) Compound

Preparation of Polymerized Silicate Composite Flocculant

Characterization and coagulation–flocculation performance of a composite coagulant: poly-ferric-aluminum-silicate-sulfate

Preparation of Poly-ferric Silicate Sulfate(PFSS)from Tetraethylorthosilicate and Its Algae Removal Performance

Characterisation and Coagulation Performance of Polysilicate-Ferric-Zinc

Properties and Coagulation Behaviour of Polyferric Silicate Sulphate by Different Preparation

Research on the preparation of composite flocculant PFMS,and its flocculating capacity

Study on Influence Factors in Flocculation Conditions of Bioflocculant

Direct preparation of polysilicic acid flocculant by using pickling waste liquor of metal plate

[The Preparation and Characterization of a New Solid Coagulant: Polymeric Ferric Silicate Sulfate].

EXTERIOR SHAPES AND COAGULATION PERFORMANCE OF SOLID POLY-FERRIC-SILICIC SULFATE

PROBING INTO THE MECHANISM OF COMPOSITE POLYALUMINUM SILICATE FLOCCULANTS WITH ION-EXCHANGE TECHNIQUE