Abstract:In this work, the hydrogen desorption properties of the novel Mg-Al-H hydrogen storage composites prepared by ball-milling the as-received magnesium hydride (MgH2) and the as-prepared aluminum hydride (AlH3) with different molar ratios (1:1, 1:0.5, and 1:0.25) are investigated systematically. Nonisothermal desorption measurements show that more than 7.51 wt % of hydrogen is released from the Mg-Al-H composites when they are heated from room temperature to 500 degrees C. Thermal analysis by differential scanning calorimeter (DSC) and hydrogen desorption spectrum by mass spectrometer (MS-H-2) are used synchronously to study the desorption process of the Mg-Al-H. The onset hydrogen desorption temperature of MgH2 in the MgH2 + AlH3 composite is dramatically reduced from 320 degrees C for the pure MgH2 to below 252 degrees C. The DSC/MS-H-2 and the X-ray diffraction (XRD) analyses show that the desorption of MgH2 in the Mg-Al-H composite is composed of two steps with the reaction between MgH2 and Al forming Mg17Al12 as the first step and the self-decomposition of the residual MgH2 as the second step. Isothermal desorptions show that the desorption kinetics of the MgH2 in the Mg-Al-H composite is significantly improved. The apparent activation energy for the desorption of MgH2 in the MgH2 + 0.25AlH(3) is reduced to 144.6 kJ/mol, which contributes to the improvement in the desorption kinetics of MgH2. The Johnson-Mehl-Avrami (JMA) kinetic studies indicate that the desorption kinetic model of MgH2 in the Mg-Al-H composite is different from the pure MgH2. Concerning the reversibility, under the conditions of 300 degrees C and 5 MPa H-2, MgH2 in the Mg-Al-H composite is almost fully recovered after absorption for 5 h while it is partially recovered for the pure MgH2. Among the samples studied, the MgH2 + 0.25AlH(3) composite exhibits the highest reversible hydrogen storage capacity of 6.10 wt % (H/M).

Hydrogen storage properties of magnesium ultrafine particles prepared by hydrogen plasma-metal reaction

Synthesis Of Mg@Mg17al12 Ultrafine Particles With Superior Hydrogen Storage Properties By Hydrogen Plasma-Metal Reaction

Synthesis and hydrogen storage properties of ultrafine Mg–Zn particles

Hydrogen Storage Behaviors and Microstructure of MF3 (m=ti, Fe)-doped Magnesium Hydride

Hydrogen desorption properties of the MgH2-AlH3 composites

Preparations and Characteristics of Ti Hydride and Mg Ultrafine Particles by Hydrogen Plasma–metal Reaction

Scaled-Up Synthesis of Nanostructured Mg-Based Compounds and Their Hydrogen Storage Properties

The Synthesis and Hydrogen Storage Properties of Pure Nanostructured Mg2FeH6

An Investigation on the Reaction Mechanism of LiAlH4–MgH2 Hydrogen Storage System

Hydrogen Sorption Behaviors of a Core–Shell Structured Mg@Fe Composite Powder (Special Issue on Advanced Materials for Hydrogen Energy Applications(2))

Hydrogen Sorption Behaviors of a Core–Shell Structured Mg@Fe Composite Powder

Realizing 6.7 wt% reversible storage of hydrogen at ambient temperature with non-confined ultrafine magnesium hydrides

Synthesis of magnesium nanoparticles with superior hydrogen storage properties by acetylene plasma metal reaction

Improved hydrogen storage properties of Mg-V nanoparticles prepared by hydrogen plasma-metal reaction

Remarkably Improved Hydrogen Storage Properties of Carbon Layers Covered Nanocrystalline Mg with Certain Air Stability

Remarkable Hydrogen Desorption Properties and Mechanisms of the Mg2FeH6@MgH2 Core–shell Nanostructure

Enhanced hydrogen storage properties of magnesium by the synergic catalytic effect of TiH 1.971 and TiH 1.5 nanoparticles at room temperature

Hydrogen desorption properties of Mg thin films at room temperature

A Comparison Study of Mg–Y2O3 and Mg–Y Hydrogen Storage Composite Powders Prepared Through Arc Plasma Method

Preparation of Mg-based hydrogen storage materials from metal nanoparticles

The Recent Progress in the Preparation of Magnesium Based Hydrogen Storage Materials by Hydriding Combustion Synthesis