Ultrafast hydrogenation of magnesium enabled by tetragonal ZrO2 hierarchical nanoparticles
X.L. Zhang,X. Zhang,L.C. Zhang,Z.G. Huang,F. Fang,J.J. Hu,Y.X. Yang,M.X. Gao,H.G. Pan,Y.F. Liu,Xuelian Zhang,Xin Zhang,Lingchao Zhang,Zhenguo Huang,Fang Fang,Jianjiang Hu,Yaxiong Yang,Mingxia Gao,Hongge Pan,Yongfeng Liu
DOI: https://doi.org/10.1016/j.mtnano.2022.100200
IF: 10.3
2022-04-01
Materials Today Nano
Abstract:Transition metal catalysts are particularly effective in improving the reaction kinetics of light metal hydrides for reversible hydrogen storage. Herein, tetragonal ZrO2 hierarchical nanoparticles (nano-ZrO2) composed of primary particles of ∼4 nm in diameter are successfully synthesized by a facile one-pot solvothermal process. The unique hierarchical structure features homogeneous distributions of in situ formed multivalent Zr-based species, which allow superior catalytic activity for hydrogen storage in MgH2. The MgH2+10 wt% nano-ZrO2 starts releasing H2 at 163 °C after one activation, which is 107 °C lower than additive-free MgH2, and 50 °C lower than that of bulk ZrO2-doped MgH2. At 230 °C, 5.9 wt% of H is rapidly liberated within 20 min from the nano-ZrO2-containing MgH2. More importantly, the material shows superior hydrogenation kinetics compared with all reported catalyst-modified MgH2. The nano-ZrO2-containing Mg took up 4.0 wt% of H in only 12 s at 100 °C under 50 bar H2, 400 times faster than the bulk-ZrO2-modified sample. Even at 50 °C, approximately 1.8 wt% H was absorbed within 1 min. Our findings provide useful insights into the design and development of high-performance catalysts toward solid-state hydrogen storage materials.
materials science, multidisciplinary,nanoscience & nanotechnology