Remarkably Improved Hydrogen Storage Properties of Carbon Layers Covered Nanocrystalline Mg with Certain Air Stability
Liuting Zhang,Nianhua Yan,Zhendong Yao,Ze Sun,Xiong Lu,Farai Michael Nyahuma,Ruihan Zhu,Guoping Tu,Lixin Chen
DOI: https://doi.org/10.1016/j.ijhydene.2020.03.170
IF: 7.2
2020-01-01
International Journal of Hydrogen Energy
Abstract:Different nanocrystalline magnesium with carbon layers were successfully synthesized via a facile wet-chemical ball milling method for 20, 30 and 40 h, respectively. Based on Scherrer formula and X-ray diffraction results, the average crystallite size of all the three samples was below 30 nm. TEM observations showed that the hydrogenated Mg particles were covered with carbon layers. Moreover, the 40 h ball milled Mg sample showed outstanding hydrogen storage performance especially in the aspect of hydrogen absorption. The as-prepared sample started to take up hydrogen at nearly room temperature and eventually absorbed 6.8 wt% hydrogen at 200 degrees C. The apparent activation energy (E-a) of hydrogen absorption for the sample was decreased to 26.7 kJ/mol, much lower than that of other reported systems. For the dehydrogenation experiments, the hydrogenated sample could start to release hydrogen at about 275 degrees C and 6.5 wt% hydrogen was desorbed in 20 min at 325 degrees C. Interestingly, the prepared samples showed noteworthy air stability. Been placed in the air for 60 min, the dehydrogenation kinetics and hydrogen capacity of the three samples were basically unchanged, making it possible to be used in future commercial applications. (C) 2020 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.