Abstract:The crystallization characteristics of LiCoO2 (LCO) thin films are key factors that affect the electrochemical properties of films. In this paper, in-situ annealed LCO films with a specific crystalline orientation were prepared on stainless steel (SS) substrates by radio-frequency (RF) magnetron sputtering. The effects of the high-temperature pretreatment of the SS substrate, substrate temperature and sputtering power on the crystallization and electrochemical properties of the LCO films were investigated in detail. It was found that the structure of the SS substrate was transformed from the gamma phase to the delta phase after the high-temperature pretreatment, and the crystallization orientation of the LCO films could be induced by the different SS phase structures. The crystallization characteristics of the LCO films were also clearly influenced by the substrate temperature. The crystallization orientation changed from the (003) orientation to the (101) orientation when the temperature increased to a high degree, but too high of a substrate temperature (such as 600 degrees C) ruptured the films. The discharge specific capacity of the LCO films increased with an increasing substrate temperature, showing a capacity of 53.8 mu Ah cm(-2) mu m(-1) at 550 degrees C and exhibiting good cycling stability. At this temperature, the crystal orientation could be controlled by adjusting the sputtering power to avoid rupturing the thin films, thereby achieving high-quality LCO films with a specific orientation. The LCO films prepared at 120 and 200 W showed obvious (101) and (003) preferred orientations, respectively. The galvanostatic charge-discharge tests showed that the (101) preferred orientation film exhibited a large initial discharge capacity of 57 mu Ah cm(-2) mu m(-1), but its cycling performance was poor. The (003) preferred orientation delivered a superior cycling performance with an initial discharge capacity of 55.6 mu Ah cm(-2) mu m(-1) and a capacity retention of 72% after 150 cycles. Cyclic voltammetry and electrochemical impedance spectroscopy measurements showed that the (101) preferred orientation was more conducive to the full infiltration of the electrolyte and the transport of lithium ions, but the stability of the structure and surface was poor and the impedance clearly increased during cycling. The (003) preferred orientation exhibited better structural and surface stability and exhibited better lithium-ion diffusion after repeated electrochemical processes.

C-Axis Textured La2CuO4thin Films Prepared by NaClO Oxidation: II. Electron Microscopic Characterization

Time Effect in Chemical Oxidation of La<sub>2</sub>CuO<sub>4</sub>Epitaxial Thin Films

The Surface Condition Effect of Cu2O Flower/grass-Like Nanoarchitectures Grown on Cu Foil and Cu Film

Induction of Superconductivity of a La 2 CuO 4 Thin Film Chemically Oxidized by NaClO

Nanocomposite-Like Structure in an Epitaxial Cacu3ti4o12 Film on Laalo3(001)

Anisotropy, band-to-band transitions, phonon modes, and oxidation properties of cobalt-oxide core-shell slanted columnar thin films

Preparation and Characterization of Α-Al2o3 Film by Low Temperature Thermal Oxidation of Al8Cr5 Coating

Microstructural and Functional Stability of Large-Scale SnO2:F Thin Film with Micro-Nano Structure

Structure and Properties of Electrocodeposited Cu-Al2o3 Nanocomposite Thin Films

Structure, Composition and Electrochemical Properties of Disordered Rock-Salt LiCoO 2 Thin Films Prepared by Ion Beam Assisted Deposition

Substrate and Thickness Effects on Structure and Transport Properties of La2/3ca1/3mno3 Films

Electrostatic Spray Assembly Of Nanostructured La0.7ca0.3cro3-Delta Films

Self-Patterned Nano Structures in Structurally Gradient Epitaxial La0.5ba0.5coo3 Films

Ag-doped La2CuO4 thin films grown on SrTiO3 substrate by laser ablation

Controllable Preparation and Electrochemical Properties of In-situ Annealed LiCoO2 Films with a Specific Crystalline Orientation on Stainless Steel Substrates

Impliance: A Next Generation Information Management Appliance

Electrostatic Spray Assembly of Nanostructured La[sub 0.7]Ca[sub 0.3]CrO[sub 3−δ] Films

Preparation and characterization of La0.5Sr0.5 CoO3 by chemical solution deposition method and its application

Chemical Structure and Interface Reaction of LaCoO3/Si Thin‐film System

Microstructure and Secondary Phases in Epitaxial LaBaCo 2 O 5.5+δ Thin Films

Crystalline Structure and Optical Properties of Cobalt Nickel Oxide Thin Films Deposited with a Pulsed Hollow-Cathode Discharge in an Ar+O2 Gas Mixture