Self-Patterned Nano Structures in Structurally Gradient Epitaxial La0.5ba0.5coo3 Films

Jie He,Jiechao Jiang,Jian Liu,Ming Liu,Greg Collins,Chunrui Ma,Chonglin Chen,Efstathios I. Meletis
DOI: https://doi.org/10.1016/j.tsf.2011.02.015
IF: 2.1
2011-01-01
Thin Solid Films
Abstract:Highly epitaxial La0.5Ba0.5CoO3 (LBCO) thin films with sharp interface and a thickness of 200nm were epitaxially grown on (001) SrTiO3 substrates using pulsed laser deposition. High-resolution transmission electron microscopy and electron diffraction analysis revealed that the films have a triple-layered structure. The first layer, close to the film/substrate interface, has a thickness of ~6nm and is a defect free single crystal disordered cubic structure (a=3.882Å) which has a lattice mismatch of −0.59% with respect to the substrate. The second layer which dominates the film structure has a single crystal disordered cubic structure (a=3.854Å) which has a lattice mismatch of −1.31% with respect to the substrate. The third layer located on the top of the film has a thickness of several nanometers and consists of 112-type ordered tetragonal structure. The cubic structures in the first and second layer have an orientation relationship of (001)LBCO//(001)STO and <100>LBCO//<100>STO with respect to the substrate. Self-patterned 3-dimensional nano structures with a dimension range from 2 to 10nm were formed in the second and third layers. These nano structures were formed by the enclosure of anti-phase boundary planes which are parallel to the {100} of the cubic structure. Epitaxial LBCO thin films with such nano structures are hard ferromagnetic with a large coercive field value and magnetoresistance effect value (~24%), and exhibit semiconductor behavior at temperatures <300K.
What problem does this paper attempt to address?