Abstract:The reduced-activation ferritic/martensitic steel, China Low-Activation Martensitic (CLAM) steel, was irradiated with single Fe, sequential He/Fe, sequential Fe/He, and simultaneous Fe+He ion beam irradiations at 350 °C–550 °C to a peak displacement damage dose of 15 dpa with 0 - 110 appm/dpa He to explore the effect of He and its synergism with displacement damage on microstructure evolution. The microstructures of all the irradiated specimens were investigated by transmission electron microscope (TEM). For Fe/He sequential irradiation, He inhibited the growth of dislocation loop induced by high-temperature He post-irradiation and reduced the number density of loops. Non-spherical He bubbles were observed only at post-injection He at 550 °C. The size of non-spherical He bubbles produced at 110 appm/dpa was about twice as large as 11 appm/dpa, and the number density increased about 6.4 times. The number density of dislocation loops induced by sequential He/Fe irradiation is the highest, and the average size of loops is comparable to that caused by simultaneous Fe+He irradiation. Moreover, the sequential Fe/He irradiation induced the lowest number density of loops of approximately 64% of the simultaneous Fe+He irradiation. The spherical bubble was observed in all irradiation with He injection above 350 °C. The average size of spherical He bubbles induced by simultaneous Fe+He irradiation is the largest, and the number density is about 2.6 times that of the sequential Fe/He irradiation. The synergisms of He in different irradiation sequences were analyzed systematically, which helps to better understand the evolutionary processes of the synergistic effect of He and displacement damage.

Proton irradiation defects in CLAM steel and their annealing behavior studied by slow positron beams

Helium Irradiation-Induced Segregation and Mechanical Response in China Low Activation Martensitic (CLAM) Steel

Microstructure Evolution and Yield Strength of CLAM Steel in Low Irradiation Condition

Microstructure and Microhardness of CLAM Steel Irradiated Up to 20.8 Dpa in STIP-V

He and H Irradiation Effects on the Nanoindentation Hardness of CLAM Steel

Mechanism analysis of grain refinement caused by deformation and the improvement of strength and ductility of CLAM steel

Microstructural Evolution of CLAM Steel under 3.5 MeV Fe 13+ Ion Irradiation

Effects of Hydrogen Charging on Mechanical Properties of CLAM Steel at Different Strain Rates

Tensile Properties of Clam Steel Irradiated Up to 20.1 Dpa in Stip-V

Effect of helium and its synergism with displacement damage on microstructure of CLAM steel investigated by single, sequential and simultaneous Fe and He ion irradiations

Irradiation Damage of Reduced Activation Ferritic/martensitic Steel CLAM Exposed to Low-Energy High-Flux D + He Mixture Plasma

Irradiation-induced Hardening and Softening of CLAM Steel under Fe Ion Irradiation

Effect of Post Weld Heat Treatment on the Microstructure and Properties of Laser-TIG Hybrid Welded Joints for CLAM Steel

Effect of Strain Rate on the Mechanical Properties of Clam Steel in Liquid Pbli Eutectic

Microstructure evolution and lead-bismuth eutectic corrosion behavior of 11Cr1Si ferritic/martensitic steel after proton irradiation

Effects of Yttrium and Heat Treatment on the Microstructure and Mechanical Properties of CLAM Steel

Hardening and Creep of Ion Irradiated CLAM Steel by Nanoindentation

Preliminary Experiments on the Corrosion of CLAM Steel in Flowing Eutectic LiPb

Stabilities of the precipitates in CLAM steel during 30,000 h thermal aging

Correlation between microstructure and hardening of 9Cr ferritic/martensitic steels irradiated in spallation neutron source

Experiments on the Magnetostriction Properties of the China Low Activation Martensitic Steel