Abstract:A cermet inert anode of 10%Ag?NiFe2O4/NiO was prepared by powder metallurgical method.The inert anode is a cylinder with 50 mm height and 50 mm diameter.It was applied to aluminium electrolysis testing for 10 h at 960℃ and the current density of 0.8 A/cm2.The behavior of inert anode for aluminium electrolysis in Na3AlF6?5%CaF2?5%Al2O3 was studied.After 10 h electrolysis,the anode was slightly corroded.It was in good condition without tumescence and scaling,which shows that the anode has good corrosion resistance to molten cryolite-based melt.The corrosion rate of the anode was estimated as about 13 mm/a and the purity of the deposited aluminium was 92%～93%.The surface of the inert anode was analyzed using energy-dispersive X-ray microanalysis.The results indicate that non-stoichiometric dissolution of the oxide phase occurred,and Fe2O3 dissolved prior to NiO and entered the electrolyte.The content of oxygen on the surface of the inert anode facing to cathode was more than that of the other side,which indicates that the reaction of O2 releasing is more acute between the two electrodes.A part of released O2 reacted with Ag on the surface of inert anode to produce Ag3O4.The section of the inert anode was also analyzed.It was found that the electrolyte penetrated into the inert anode and reacted with Fe2O3,then the product FeF3 deposited in the interspaces in the anode.

Effect of Electrolysis Superheat Degree on Anticorrosion Performance of 5Cu/(10nio-Nife2o4) Cermet Inert Anode

Effect of cu content on the corrosion behaviour of Cu/(10NiO-9ONiFe(2)O(4)) cermets in aluminum electrolysis

Effect of Cu content on the corrosion behaviour of Cu/(10NiO-90NiFe 2O4) cermets in aluminum electrolysis

Effect of Metallic Phase Species on the Corrosion Resistance of 17M/(10nio-Nife2o4) Cermet Inert Anode of Aluminum Electrolysis

Anodic Corrosion Behavior of NiFe 2 O 4 -Based Cermet in Na 3 AlF 6 -K 3 AlF 6 -AlF 3 for Aluminum Electrolysis

Anodic Corrosion Behavior of NiFe2O4-Based Cermet in Na3AlF6-K3AlF6-AlF3 for Aluminum Electrolysis

Effect of Ni Content on Corrosion Behavior of Ni/(10nio-90nife(2)O(4)) Cermet Inert Anode

Effect of Operating Parameters on Corrosion Behavior of NiFe2O4 Cermet Inert Anodes

On the corrosion behaviour of NiFe2O4-NiO based cermets as inert anodes in aluminum electrolysis

Effect of Operating Parameters on CorrosionBehavior of NiFe_2O_4 Cermet Inert Anodes

On the Corrosion Behaviour of Ni-Nio-Nife(2)O(4) Cermets As Inert Anodes in Aluminum Electrolysis

Materials Fabrication and Corrosion Behavior of NiFe2O4 Cermet Inert Anodes

Effect of Additive BaO on Corrosion Resistance of Xcu/(10nio-Nife2o4) Cermet Inert Anodes for Aluminum Electrolysis

Investigation of 5Cu-(10NiO-NiFe2O4) inert anode corrosion during low-temperature aluminum electrolysis

Electrolysis Corrosion Behaviour of NiFe2O4-based Cermet Inert Anode

Effect of coated spinel NiFe_2O_4 in the surface of metal phase 20Ni-80Cu on corrosion resistance of 15(20Ni-80Cu)/85(NiFe_2O_4-10NiO) cermet for aluminum electrolysis

Preparation and Chemical Corrosion of Behaviour Cermet Inert Anode Used in the Aluminum Smelter

Results from 100 H Electrolysis Testing of NiFe2O4 Based Cermet As Inert Anode in Aluminum Reduction

Effect of coated spinel NiFe204 in the surface of metal phase 20Ni-80Cu on corrosion resistance of 15（20Ni-80Cu）/85（NiFe20~-10NiO） cermet for aluminum electrolysis

Preparation of a cermet inert anode based on ferrous nickel and its use in an electrolysis study

CORROSION BEHAVIORS OF NiFe2O4-NiO-Co3O4 INERT ANODE MATERIALS IN Na3AlF6-Al2O3 MELTS