Anodic Corrosion Behavior of NiFe 2 O 4 -Based Cermet in Na 3 AlF 6 -K 3 AlF 6 -AlF 3 for Aluminum Electrolysis

Zhongliang Tian,Yanqing Lai,Shu Yang,Jie Li,Jiann-Yang Hwang,Yexiang Liu
DOI: https://doi.org/10.1007/s11663-015-0328-8
2015-01-01
Metallurgical and Materials Transactions B
Abstract:A (Cu,Ni)/(10NiO-NiFe 2 O 4 ) cermet was tested as an inert anode for aluminum electrolysis in Na 3 AlF 6 -K 3 AlF 6 -AlF 3 melt at 1173 K (900 °C), and its corrosion behavior was studied. The results show that the low-temperature Na 3 AlF 6 -K 3 AlF 6 -AlF 3 bath is beneficial, improving the service conditions. With the combined effects of the electrolyte composition and the nascent oxygen during electrolysis, the metal phase (Cu,Ni) at the surface of anode will not be leached preferentially, but be transferred into the aluminates including FeAl 2 O 4 , NiAl 2 O 4 and CuAl 2 O 4 . This is helpful for the anode to improve its corrosion resistance.