Preparation of a cermet inert anode based on ferrous nickel and its use in an electrolysis study

Luo Tao,WangZhao Wen,GaoBing Liang,YuXu Guang,QiuZhu Xian
2005-01-01
Abstract:Hot press-sintering was adopted to fabricate inert cermets anodes based on the nickel ferrite for use in aluminum electrolysis research. The relative density of the anodes was more than 98% and the electrical conductivity increases with increasing temperature and ranged from 40 Omega(-1) (.) cm(-1) to 80 Omega(-1) (.) cm(-1) at 900 degrees C. The electrolysis experiments with the cermet anodes were run at different anodic current density. The amount of contamination in the aluminium produced increased with increasing anodic current density, and the amount of contaminants (Fe, Ni and Cu) is < 0.257wt% at 0.8A/cm(2). The main reasons for anode corrosion are the ascending activity of Fe(3+) ions and enrichment of Cu in the outer anode due to the increasing anodic current density.