Abstract:Direct laser sintering of metal powder is a promising manufacturing process to produce rapid moulds (or rapid tooling) because complex three-dimensional (3-D) metal parts can be created directly from computer-aided design (CAD) data without machining or use of additional tooling. However, material and process are still the crucial issues that restrict its wider adoption although the technology has been introduced more than 7 years. This paper characterises a self-developed Cu-based metal powder used for direct laser sintering. The material system is Cu-based alloy metal powder, which consists of two metal powders: high-purity Cu powder and pre-alloyed SCuP metal powder. The scanning electron microscope (SEM), XRD and energy dispersive X-ray (EDX) analyses show that the bonding mechanism of this process is liquid-phase sintering. The pre-alloyed SCuP metal powder with lower melting point (645°C) acts as the binder during laser sintering, while the Cu powder with higher melting point (1083°C) acts as the structure. The element phosphorus in the powder can act as flux to protect the Cu oxidisation. A case study on fabricating the inserts of a mobile phone cover mould was also carried out. The inserts were created in ambient atmosphere at room temperature. The total sintering time is 40h. Sixty five percent relative theoretical density and average surface roughness Ra 14–16μm were achieved with negligible distortion and curling. Epoxy infiltration was employed as post-process to improve the density and the strength of the sintered tooling. The mould inserts were used to inject ABS-PC mobile phone cover after polishing. No defects were found after moulding of 500 components.

Rapid prototyping manufacturing of silica sand patterns based on selective laser sintering

Study on the Process Parameters of Selective Laser Sintering Foundry Silica Sands

Rapid Casting Technology Based on Selective Laser Sintering

Surface Roughness Control of Root Analogue Dental Implants Fabricated Using Selective Laser Melting

Material optimization and post-processing of sand moulds manufactured by the selective laser sintering of binder-coated Al2O3 sands

POLYMER-DERIVED SIC CERAMIC WITH TRIPLY PERIOD MINIMAL SURFACE STRUCTURE FABRICATION THROUGH DIGITAL LIGHT PROCESSING

Rapid prototyping of porcelain products by layer-wise slurry deposition (LSD) and direct laser sintering

Effects of process parameters on dimensional precision and tensile strength of wax patterns for investment casting by selective laser sintering

Rapid manufacturing of silica glass parts with complex structures through stereolithography and pressureless spark plasma sintering

Comparisons of Indirect Selective Laser Sintering with Selective Laser Melting

Multiphase Polymeric Materials for Rapid Prototyping and Tooling Technologies and Their Applications

Development of the Machines and Materials for Rapid Prototyping & Tooling Technologies and 3D Measurement in Huazhong University of Science and Technology

Research and implementation of large-area sintering technology based on image-shaped laser

Rapid and high-accuracy forming of ceramic parts by DLP technology based on optimization of shear stress

Fiber Laser and Its Applications in Rapid Prototyping of Selective Laser Melting

Research on Selective Laser Melting System and Technologic Experiment

Research on the Rapid-precision Casting Precess Based on the Rapid Prototyping Technology

Effects of Processing Parameters on Rapid Manufacturing 90w–7ni–3fe Parts Via Selective Laser Melting

Development and characterisation of direct laser sintering Cu-based metal powder

Fabrication of Al2O3‐SiO2 Ceramics Through Combined Selective Laser Sintering and SiO2‐sol Infiltration

Rapid Prototyping of Piezoelectric Ceramics Via Selective Laser Sintering and Gelcasting