Research on the Rapid-precision Casting Precess Based on the Rapid Prototyping Technology

Yilin Qu,Dichen Li
2006-01-01
Abstract:Preparation of moulding shell used Stereolithography Apparatus prototypes as the moulds was discussed.The experimental results indicates that mixture of silica powder 100,Na5P3O1 3,Li bentonite 2,20%PVB solution 7,tiny JFC and appropriate amount methanol could served as the refractory slurry,the refractory slurry was coated and silica grains was scattered on the prototypes for several times until 5~10 mm thickness of moulding shell,then baked at 35 ℃ for 8 to 10 hr.,come into furnace for baking in 300 ℃,and the temperature of furnace was increased to 950 ℃ by 300 ℃/h,kept for 30 min and cool off,the moulding shell was ready.silica powders was replaced by other refractory,and formula was readjusted slightly,the mixtures could use for many alloys castings.