Abstract:A LiFePO4/C composite was synthesized by a simple solid-state reaction method using glucose as reductive agent and carbon source and FePO4 as precursor, which was prepared by introduction of Na3PO4 as phosphorus source and pH regulator in order to pursue lower cost and environmental protection. The structure and morphology of FePO4 and LiFePO4/C were investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Furthermore, electrochemical performance of LiFePO4/C was investigated by galvanostatic charge–discharge tests and cyclicvoltammogram (CV). The results indicate that FePO4 obtained has a small particle size and uniform particle distribution, which is demonstrated to be applicable as the iron source to synthesize LiFePO4/C. Prepared LiFePO4/C shows an excellent rate capability and cycle performance. At rates of 0.1 C, 0.2 C, 1 C and 2 C, the initial discharge capacities of 161, 158, 145 and 120 mAh/g were achieved, respectively and the discharge capacity is 154, 153, 140 and 116 mAh/g after 400 cycles. The employed method of preparing FePO4 by introduction of Na3PO4 has advantages such as low cost, safe raw material, environmental benign and recyclable products, which is suitable for industrial production.

Preparation of Precursor and Performance of LiFePO4

Rapid Preparation of High Electrochemical Performance LiFePO4/C Composite Cathode Material with an Ultrasonic-Intensified Micro-Impinging Jetting Reactor

Preparation and Performance of FePO_4 Precursor for LiFePO_4

Preparation of Precursor FePO4 and Its Effects on Electrochemical Properties of LiFePO4

SYNTHESIS AND CHARACTERIZATION OF <font>LiFePO</font><sub>4</sub>/<font>C</font> PREPARED VIA A SOL–GEL METHOD

Effect of precursor FePO_4·2H_2O on electrochemical properties of LiFePO_4

Preparation and Characterization of LiFePO[sub 4] from a Novel Precursor of NH[sub 4]fepo[sub 4]⋅h[sub 2]O

Preparation and Electrochemical Performance of LiFePO_4/C Using Fe_2O_3 As Raw Material

Synthesis And Electrochemical Characteristics Of Lifepo4/C Cathode Materials From Different Precursors

Preparation and Characterization of LiFePO4 Made from NH4FePO4·H2O

Synthesis and Characterization of Lifepo4/C Prepared Via A Sol-Gel Method

Preparation of LiFePO_4 by solution evaporating method and its performance research

Preparation and characterization of LiFePO4 made from NH4FePO4 center dot H2O

Morphology and Reaction Mechanism of LiFePO4 Prepared by Hydrothermal Synthesis

Research on Preparation of Nano-porous Lithium Iron Phosphate for Lithium-ion Battery Electrode Materials

Preparation And Characterization Of Lifepo4 From A Novel Precursor Of Nh4fepo4 Center Dot H2o

Preparation and Electrochemical Performance of Spherical LiFePO4

The preparation and characterization of LiFe0.98Mn0.02PO4/C by spraydrying and low temperature reduction route

Preparation and Electrochemical Properties of High-performance LiFePO_4

Preparation of LiFePO4 with inverse opal structure and its satisfactory electrochemical properties

An Improved Method to Prepare FePO4 by Introduction of Na3PO4 and Its Usage for Fabricating LiFePO4