Phase Relations and Microwave Dielectric Properties of Vanadium Modified Ba5Nb4O15 Ceramics

Fei Zhao,Hao Zhuang,Zhenxing Yue,Jing Pei,Zhilun Gui,Longtu Li

DOI: https://doi.org/10.1016/j.matlet.2006.11.095

IF: 3

2007-01-01

Materials Letters

Abstract:Microwave dielectric ceramics of Ba5Nb4-xVxO15 (x=0-1) were prepared by a solid-state reaction method. Vanadium substitution can markedly lower the sintering temperature of Ba5Nb4O15 from 1450 to 1100 degrees C. The X-ray powder diffraction analysis reveals the multiphase nature of this system. A hexagonal-to-orthorhombic phase transition was also observed for the BaNb2O6 secondary phase. The microwave dielectric properties, such as tau(f), epsilon(r) and Q x f value, decreased with increasing vanadium content for samples sintered at I 100 degrees C. There was an apparent increase in tau(f) and Q x f value for samples (x >= 0.5) sintered at 1200 degrees C due to the hexagonal-to-orthorhombic phase transition of the BaNb2O6 phase. These results suggested that the microwave dielectric properties of multiphase ceramics strongly depended on the phase compositions and the phase transitions. (C) 2006 Elsevier B.V. All rights reserved.