Abstract:Four layer-structured Sodium Bismuth Titanate Aurivillius ferroelectric ceramics with composition Na 0.5 Bi 4.5− x La x Ti 4 O 15 ( x = 0.0, 0.25, 0.5, 0.75 and 1.0) were prepared using conventional solid state reaction method. The existence of main diffraction peak (119), confirms the four layer structure which corresponds to the highest diffraction peak (112 m + 1) observed in typical BLSF's XRD pattern. The co-existence of orthorhombic and tetragonal symmetry is validated with splitting observed in diffraction peak (200/020) and merging of these diffraction peaks at La rich compositions advocate structural transformation leading towards tetragonal symmetry. Williamson–Hall method was used to enumerate the crystallite size and micro strain, with the appropriate consideration of peak broadening parameters of individual peaks. Plate like grain evolution in microstructure of prepared samples were identified with images obtained from Field emission scanning electron microscope (FESEM). Deconvolution of the obtained Raman curves were done into their individual Gaussian components and different modes were obtained around 78, 102, 142, 221, 265, 345, 462, 552 ,736 and 854 cm −1 . The modes obtained below 200 cm −1 are low frequency modes which are assumed to be due to A-site distortion and modes obtained above 200 cm −1 are high frequency modes which are due to tilting and rotation of TiO 6 octahedron. The blue shifting of vibrational modes attribute to substitution of heavier Bi 3+ (208.9 amu) ions with comparatively lighter element La 3+ (138.9 amu). The present study revealed that presence of La ions in four layer structured lead to tetragonal symmetry and optimum polarizability can be achieved with selective concentration of La ( x = 0.75 ) in present BLSF.

Raman Scattering Study of La-, Nd- and Sm-Substituted Bi4ti3o12

Lanthanum distribution in SrBi4−xLaxTi4O15

Structure analysis and Raman spectroscopy of La-doped Na0.5Bi(4.5−x)LaxTi4O15 ceramics

Study of A-site doping of SrBi4Ti4O15 Bi-layered compounds using micro-Raman spectroscopy

Structural Phase Transition Due to La Substitution in Bi4ti3o12

La3+ Substitution in Four-Layers Aurivillius Phase Srbi4ti4o15

Raman Spectroscopy and X-ray Diffraction Study of Sol–gel Derived (pb1−xlax)ti1−x/4o3 Thin Films on Si Substrates

Effect of Li doping and Li, La co-doping on the structure and physical properties of LaBa2Cu3Oy

Raman Spectra of Srm-3Bi4TimO3m+3 Thin Films

Structural and vibrational properties of (Bi1−xLax)FeO3 and (Bi1−yBay)(Fe1−yTiy)O3 multiferroic ceramics investigated by Raman scattering

Ferroelectric and Dielectric Properties of La/Mn Co-Doped Bi4ti3o12 Ceramics

Variable-temperature Raman scattering and X-ray diffraction studies of Bi3.25Nd0.75Ti3O12 ceramics

Study on ferroelectric and dielectric properties of La-doped SrBi4Ti4O15 ceramics

Tuning the Structural and Optical Properties of Bismuth Titanate by Different Nd Substitution Content

Substitution of Sm3+ and Nd3+ for Bi3+ in SrBi8Ti7O27 Mixed Aurivillius Phase

Substitution of Sm<sup>3+</sup> and Nd<sup>3+</sup> for Bi<sup>3+</sup> in SrBi<sub>8</sub>Ti<sub>7</sub>O<sub>27</sub> Mixed Aurivillius Phase

Raman-active phonons in Bi2Sr2−xLaxCaCu2Oy: effect of the oxygen content induced by La doping

Dielectric properties of La3+ substituted BaBi8Ti7O27 ceramics

Effects of Sm/Bi co-substitution on microstructures and microwave dielectric characteristics of Ba6−3xLa8+2xTi18O54 (x = 2/3) solid solution

Structures and Dielectric Properties of La-Substituted SrBi8Ti7O27 Ceramics

X-ray Diffraction and Raman Scattering Study of SrBi2Ta2O9 Ceramics and Thin Films with Bi3TiNbO9 Addition