Substitution of Sm3+ and Nd3+ for Bi3+ in SrBi8Ti7O27 Mixed Aurivillius Phase

R. Z. Hou,X. M. Chen,S. Y. Wu

DOI: https://doi.org/10.1143/jjap.42.5169

2003-01-01

Abstract:Sm3+ and Nd3+ substitution for Bi3+ in SrBi8Ti7O27 with mixed layer structure was investigated. The solid solution limit of Sr(Bi1-xSmx)8Ti7O27 was between x=0.15 and x=0.25 while that of Sr(Bi1-xNdx)8Ti7O27 was between x=0.05 and x=0.15. The temperature stable dielectric ceramics with high dielectric constants (>100) were obtained by Sm3+ and Nd3+ substitution for Bi3+ in SrBi8Ti7O27, where the dielectric loss varied from 0.002 to 0.02 at 1 MHz.