Abstract:Metal matrix composites are of interest every day due to their lightweight, improved mechanical properties, and increased corrosion resistance. They are used in the aeronautical, aerospace, marine, and automotive industries. A variety of methods can estimate Their corrosion properties. The open-circuit potential studies are also a tool for evaluating the corrosion of composite materials. This research paper focuses on studying open circuit potential determination of the aluminium 7075 alloys reinforced with silicon carbide particulate in differently concentrated sodium hydroxide solutions. The composite materials were prepared by adding 2, 4, 6, 8 and 10 weight percentages of silicon carbide to the aluminium base metal liquid melt metallurgy technique (Vortex method). The silicon carbide used as reinforcement in size range of 50 – 80 μm, which is commercially available. The SiC particulates material is had been preheated to 400°C and introduced into the liquid melt of Al7075 at a rate of 100 g/m, under constant agitating condition using a mechanical stirrer system for 3 to 4 minutes. Rectangular specimens of 2 cm length, 1cm width and 1 mm thickness were used for the experiments. 1sq.cm area of the specimens was exposed to sodium hydroxide medium. Open circuit potential experiments test was conducted using a multimeter and calomel electrode system. The potential observed for 2, 4, 6, 8 and 10% silicon carbide composites were less than the potential of matrix alloy for a range of 30 hours.

Corrosion Behaviour of Porous SiAlON Ceramics

In-situ Grown Columnar Mullite Reinforced SiC Porous Ceramic Membrane Support with Excellent Mechanical Performance and Corrosion Resistance: Using TiO2 As the Key to Form Columnar Mullite

Corrosion Resistance Properties of Porous Alumina–Mullite Ceramic Membrane Supports

Corrosion Resistance Characterization of Porous Alumina Membrane Supports

Study on Resistance to Erosion of Cordierite and Alumina Supports

Corrosion and Oxidation of Silicon Carbide Based on a Nitride Binder in an Aluminum Electrolyzer Side Lining

Corrosion behavior of Al4SiC4/SiC ceramics exposed to molten calcium‐magnesium‐alumino‐silicate at 1350°C in air

Porosity and Oxide Layer Dependence of Thermal Shock Behavior of Porous Silicon Nitride Ceramics

Corrosion Behavior of SiC_w?Al Compoite

Comparison of Hydrothermal Corrosion Behavior of SiC with Al2O3 and Al2O3 + Y2O3 Sintering Additives

Elaboration and Chemical Corrosion Resistance of Tubular Macro-Porous Cordierite Ceramic Membrane Supports

Internal Friction Behavior Of Sic Ceramics Subjected To Water Vapor Corrosion

Progress in Preparation and Properties of Porous Silicon Nitride Ceramics

Corrosion mechanism of Al2O3–SiC–C refractory by SiO2–MgO-based slag

Permeating behaviour of porous SiC ceramics fabricated with different SiC particle sizes

Studies on the corrosion resistance of Al7075 / SiC metal matrix composites in an alkaline environment

Effect of Abrasive Particle Size on Anti-Abrasion Performance of Si3N4 Ceramics

The corrosion resistance mechanisms of the cr-coated SiC in molten Na2SO4 salt: Strengthened boundaries and protective scales

Effects of chemical corrosion and thermal shock on the properties of mullite- and cordierite-bonded porous SiC ceramics prepared using waste fly ash

Oxidation behavior of SiC‐AlN ceramics exposed to dry oxygen and water oxygen environments at 1100–1300°C

High-strength and corrosion-resistant Al2O3 ceramics with excellent closed-cell structure