Abstract:In recent publications, we have proposed a model of fatigue damage to steels under multicyclic loading of smooth specimens and dependencies to describe the kinetics of fatigue limit reduction as a damage parameter. Such a decrease is due to the initial fatigue damage of the material at the microstructure level, which leads to the incubation of a crack in the zones of microstructural stress concentrators or its weakest elements, followed by germination along crystallographic planes and then by the transition to growth along forced planes under the action of normal stresses. In the currently known studies, fracture mechanics methods adapted to the growth of short cracks describe fatigue damage at the initial stages of fatigue. Their practical application is complicated by the need to determine the specific characteristics of the microstructure of materials, which are only sometimes available and unambiguous. In this regard, we consider a phenomenological approach based on the assumption of continuous fatigue damage of a material from the beginning of its cyclic loading until fracture or until the initiation of a non-propagating crack at the endurance limit. This damage can be described by a drop in the initial endurance limit to its standardized value at the French line and then to the level determined by the size of the crack at the fracture of the specimen. As the crack grows from the French line to fracture, the endurance limit corresponds to the threshold stress in the terminology of fracture mechanics. To describe the change in the endurance limit, a dependence is proposed that uses the parameters of the fatigue curve. A similar relationship is used to describe crack growth, which causes a decrease in the endurance limit.

Analyses of the fatigue crack propagation process and stress ratio effects using the two parameter method

On the Study of Fatigue Crack Propagation in the Time Domain

Depth-sensing Indentation Measurement and Finite Element Analysis of Residual Stress Field Near Fatigue Crack Tip

Microscopic Analysis by EBSD Method on Fatigue Crack Propagation Behaviour in Ultrafine-Grained Copper

A Simple Engineering Approach in the Prediction of the Effect of Stress Ratio on Fatigue Threshold

Analysis of the relationship between Kmax and ΔKth for aluminium alloys

An analysis of fatigue crack features at various crack lengths through mating fracture surface pairs

Statistical Analysis Methods of Fatigue Crack Growth Rate

Analysis of the Effect of K-Max on the Fatigue Crack Propagation Threshold

Effect of loading conditions on short fatigue crack propagation behaviours in cast Al Si alloys

In-situ observation of strain evolution and ratchetting of growing fatigue cracks

Crystallographic analysis on small fatigue crack propagation behaviour of a nickel‐based single crystal superalloy

A NOVEL PARAMETER FOR EVALUATING THE FATIGUE CRACK GROWTH RATE IN CARBON STEELS

Microstructurally small fatigue crack growth rates in aluminium alloys for developing improved predictive models

In situ SEM-DIC technique and its application to characterize the high-temperature fatigue crack closure effect

EVALUATION OF SMALL CRACK GROWTH RATE OF ALUMINUM ALLOYS UNDER DIFFERENT STRESS GRADIENTS

Computational Monitoring of an Initial Fatigue Crack Incubation and Growth in a Smooth Specimen

Low-cycle Fatigue Small Crack Initiation and Propagation Behaviour of Cast Magnesium Alloys Based on In-Situ SEM Observations

Study on the crack nucleation mechanism of Ti-2Al-2.5Zr alloy in low cycle fatigue: Quasi in-situ experiments and crystal plasticity simulation

Application of a New, Energy-Based ΔS* Crack Driving Force for Fatigue Crack Growth Rate Description

The effect of frequency on fatigue crack propagation rate and striation spacing in 2024-T3 aluminium alloy and SM-50 steel