Abstract:Most commercial high-temperature superconducting coated conductors based on ion beam assisted MgO deposited templates use $\mathrm{LaMnO_3}$ (LMO) films as the terminating buffer layer. In contrast, coated conductors based on inclined substrate deposition (ISD)-MgO technology are still produced with homoepitaxial (homoepi)-MgO as the cap layer. In this work we report on the deposition of LMO buffer layers on ISD-MgO/homoepi-MgO by electron beam physical vapor deposition. The growth parameters of textured LMO films were studied systematically and their properties were optimized regarding the critical current densitiy ($J_\mathrm{c}$) of the subsequently deposited $\mathrm{DyBa_2Cu_3O}_{\mathrm{7-}\delta}$ (DyBCO) superconducting films. LMO films without outgrowths at the surface were obtained at growth rates of up to $4\,\mathrm{Å/s}$. Despite the formation of non-stoichiometric LMO films containing $59\,\%$ La, single-phase films were obtained at substrate temperatures below $775^{\circ}\mathrm{C}$ and at oxygen partial pressures of up to $4\times10^{-4}\,\mathrm{mbar}$ due to a large homogeneity region towards La. The $J_\mathrm{c}$ values of DyBCO films deposited on LMO were found to be independent of the LMO thickness in a range from $50\,\mathrm{nm}$ to $450\,\mathrm{nm}$. DyBCO films on LMO reach $J_\mathrm{c}=0.83\,\mathrm{MA/cm^2}$ at $77\,\mathrm{K}$ in zero applied field. This value is up to $30\,\%$ higher than those of DyBCO films grown directly on homoepi-MgO. The wide range of LMO growth parameters and higher $J_\mathrm{c}$ values of DyBCO on LMO compared to DyBCO on homoepi-MgO make this material attractive for its use in manufacturing coated conductors based on ISD-MgO technology.

Chemical Solution Deposition of Lamno3-Based Films for Coated Conductors

Orientation, microstructure and transport properties of chemical solution deposition prepared La2/3Ca1/3MnO3 and La2/3Ca1/3MnO3/La0.8Na0.2MnO3 films

Fabrication of La0.8na0.2mn1-Xcuxo3 (X=0, 0.05) Thin Films on Ysz Substrates Via Chemical Solution Deposition

Orientation Control of Chemical Solution Deposited Lanio3 Thin Films

Preparation of La0.7Sr0.3Mn1+xOy (1 ⩽ X ⩽ 4) Thin Films by Chemical Solution Deposition: Dual Epitaxy and Possible Spinodal Growth

Seed layer, solution concentration and thickness effects on CSD-derived La2Zr2O7 buffer layers for coated conductors

Preparation And Characterization Of Chemical Solution Derived Templates For Coated Conductors

Chemical Solution Processing and Characterization of Highly Oriented (ba,ln)nb2o6[ln: La, Gd, Dy] Thin Films

Tuning The Magnetic And Transport Properties Of La0.8ca0.2mno3 Films By Ba0.8sr0.2tio3 Intercalated Layers Grown With Polymer-Assisted Deposition

Insight into the Enhancement of Transport Property for Oriented La0.9MnO3 Films

Metal Organic Deposition of Lanthanum Zirconate Buffer Layer on Biaxially Textured Ni-5%W Substrate

Tailoring the Crystallographic Orientation of MOD-derived La2Zr2O7 Buffer Layers for Coated Conductors

Preparation of epitaxial La2-xGdxZr2O7 buffer layer for coated conductors using sol-gel method

Chemical Solution Deposition Derived (001)-Oriented Epitaxial BiFeO3 Thin Films with Robust Ferroelectric Properties Using Stoichiometric Precursors (Invited)

Synthesis of Conductive Lanio3 Thin Films by Chemical Solution Deposition

Chemically Deposited (100)-Oriented BaTiO3 Films with Highly Concentrated Solution Using High Crystallinity BaTiO3 As a Buffer Layer

Growth of Thick La2Zr2O7 Buffer Layers for Coated Conductors by Polymer-Assisted Chemical Solution Deposition

Preparation and characterization of La0.5Sr0.5 CoO3 by chemical solution deposition method and its application

The Preparation and Demonstration of Epitaxial La0.67Sr0.33MnO3−δ Films/((110) Orientation)

$\mathrm{La}_{\mathrm{1-}x} \mathrm{Mn}_{\mathrm{1-}y} \mathrm{O}_{\mathrm{1\pm}δ}$ buffer layers on inclined substrate deposited MgO templates for coated conductors

Chemical Solution Deposition of Transparent and Metallic La0.5Sr0.5TiO3+x/2 Films Using Topotactic Reduction