Abstract:The C=C double bonds in the main chain of hydroxyl-terminated polybutadiene (DHTPB), obtained by the degradation of polybutadiene rubber, were partially epoxided using m-chloroperoxybenzoic acid (mCPBA) as epoxidation reagent. A series of epoxided HTPBs (EHTPB) with different epoxy contents (5%, 10% and 15%) were prepared by tuning the molar ratio of mCPBA to C=C double bonds. The structures of EHTPBs were characterized by Fourier transform-infrared (FTIR), nuclear magnetic resonance (H-1-NMR) spectroscopy and gel permeation chromatography (GPC). The epoxy percent in EHTPBs from H-1-NMR spectra was in accordance with the design. In addition, a series of EHTPB-based polyurethane elastomers (EPU) were prepared by the reaction between EHTPB and 4,4'-diphenylmethane diisocyanate with 1,4-butanediol as a chain extender. Mechanical and thermal properties of the EPU samples were characterized by tensile test, differential scanning calorimetry (DSC) and thermal gravity analysis (TGA). With increased epoxy percent in EHTPB, the Young's modulus and the tensile strength of the EPU samples increased, whereas the elongation at break decreased. The sample EPU10 prepared with 10% of epoxy had the best mechanical properties with 8.82 MPa as Young's modulus, 7.83 MPa as tensile strength, and (485 +/- 23)% as elongation at break. The elasticity recovery of the EPU sample was slightly better than HTPB-based PU (EPU0). The results with TGA test showed that the thermal degradation of EPU, similar to EPU0, was divided into three stages. However, the EPU samples had better thermal stability with the initial degradation temperature at 210 degrees C, about 30 degrees C higher than that of EPU0. The DSC results showed that the glass transition temperature (T-g) of EPU gradually increased as epoxy percent was increased, though still lower than that of HTPB (FHTPB) based PUs prepared by free-radical polymerization.

Properties of Poly(butylene Terephthalate) Chain‐extended by Epoxycyclohexyl Polyhedral Oligomeric Silsesquioxane

Synthesis and Thermomechanical and Rheological Properties of Biodegradable Long-Chain Branched Poly(Butylene Succinate-Co-Butylene Terephthalate) Copolyesters

Preparation and Properties of Epoxided Hydroxyl-terminated Polybutadiene Based Polyurethane Elastomers

Biobased flexible aromatic polyester poly(1,5-pentylene terephthalate) (PPeT): Revisiting melt crystallization behaviors and thermo-mechanical properties

Chain Extension Of Poly(Butylene Terephthalate) By Reactive Extrusion

Synthesis, characterization and lubricating effect of long chain branched polydimethylsiloxane-g-polyethylene copolymers

Thermal and Mechanical Properties of Poly(butylene Terephthalate)/epoxy Blends

Chain Extension of Polyester PBT with Epoxide Resin

Toughening of PBT by POE/POE-g-GMA Elastomer Through Regulating Interfacial Adhesion and Toughening Mechanism

Preparation of PBT/POE‐g‐GMA/PP Ternary Blends with Good Rigidity–toughness Balance by Core–shell Particles

Preparation and Properties of Ethylene Octane Copolymer Blends with High Strength and Polarity

Toughening of Polylactide with Epoxy-Functionalized Methyl Methacrylate-Butadiene Copolymer

Porous Melt Blown Poly(butylene terephthalate) Fibers with High Ductility and High-Temperature Structural Stability

Toughened poly(butylene terephthalate) by epoxided ethylene-propylene-diene-rubber

PBT-b-PEO-b-PBT triblock copolymers: Synthesis, characterization and double-crystalline properties

Chain Extension of Polybutylene Adipate and Polybutylene Succinate with Adipoyl‐ and Terephthaloyl‐biscaprolactamate

Catalyzed Chain Extension of Poly(butylene Adipate) and Poly(butylene Succinate) with 2,2′‐(1,4‐Phenylene)‐bis(2‐oxazoline)

Reinforcing and Toughening Modification of PPC/PBS Blends Compatibilized with Epoxy Terminated Hyperbranched Polymers

Investigation of the Properties of PBT/ABS-g-GMA Blends Modified with Epoxy Resin of Mid-Molecular Weights

Effect of chain extender on the morphological, rheological and mechanical properties of biodegradable blends from PBAT and P34HB

Preparation and Properties of Poly(Ethylene Terephthalate)/Poly(Butylene Terephthalate) Alloys with High Toughness