Abstract:The particle size grade combination of silicon powder of 40μm, fine Si3N4 powder of 0.5μm, Al2O3 and MgO powder of 5μm was studied and the highest density of both green compact and the final ceramic could be obtained when the silicon, Si3N4, Al2O3 and MgO powder were mixed in a weight ratio of 75:25:1:1. The SiC powder of 45nm was introduced into the compacts according to different ratio and nitrided at 1400°C for 20h. No obvious influence of the addition of SiC on the relative density of the SiC/Si3N4 ceramics was observed. SEM photographs of SiC/Si3N4 ceramics showed that needle-like β-Si3N4 crystals formed in all the SiC/Si3N4 ceramics. More and longer needle-like β-Si3N4 crystals were seen in the ceramics with the higher SiC content, and no needle-like β-Si3N4 crystals were found in the pure Si3N4 ceramic prepared by reaction bonding of silicon. A flexural strength rise with the increase of the SiC content in the SiC/Si3N4 was found. The phenomenon was attributed to the existence of more needle-like β-Si3N4 crystals with the increase of the SiC content, which could improve the flexural strength of the ceramic. As a source of SiO2, addition of nanometer SiC is helpful for the formation of needle-like β-Si3N4.

Fabrication of Reaction-Bonded SiC Ceramics by Slip Casting of SiC/C Suspension

Preparation of Complicated SiC Green Bodies via Aqueous Slip Casting

Fabrication and Properties of SiC Porous Ceramics by Slip Casting Process

Rheological Behavior of SiC Aqueous Suspension and Its Effect on the Green Body of Slip Casting

Gelcasting of Concentrated Aqueous Silicon Carbide Suspension

Preparation And Properties Of Sic Ceramics Via Sls/Cip Process

Preparation and properties of SiC ceramics <i>via</i> SLS/CIP process

Colloid and Rheological Property of the Concentrated SiC/Si Suspensions

Processing, Microstructures and Mechanical Properties of Aqueous Gelcasted and Solid-State-Sintered Porous Sic Ceramics

Processing, microstructure and mechanical properties of porous silicon nitride by a slip casting method-using petroleum coke as pore former

Properties of reaction-bonded SiC/Si3N4 ceramics

Fabrication and Properties of Reaction-Formed SiC by Infiltrating Molten Si into Mesocarbon Microbeads-Based Carbon Preform

Effect of Solid Contents and Ratio of Particles on Recrystallized SIC

Fabrication, Structure and Properties of Porous SiC Ceramics with High Porosity and High Strength

Preparation of <i>In Situ</i> Synthesized SiC Particles Reinforced Highly Porous Si<sub>3</sub>N<sub>4</sub> Ceramics by Gel-Casting

Direct Coagulation Casting of Silicon Carbide Suspension Via Polyelectrolyte Dispersant Crosslink Reaction

Co-Deposition of Binary Particles During Slip Casting Process

Preparation of in-situ synthesized SiC particles reinforced highly porous Si3N4 ceramics by gel-casting

Study On Gelcasting Of Silicon Carbide

Porous SiC/SiCN Composite Ceramics Fabricated by Foaming and Reaction Sintering

Fabrication and Mechanical Properties of SiC Reinforced Reaction-Bonded Silicon Nitride Based Ceramics