Abstract:An initially single phase high entropy alloy (HEA) Al0.3CoCrFeNi was irradiated by 3 MeV Au ions to a fluence of 6 x 10(15) cm(2) (similar to 31 dpa at damage peak) at four different temperatures ranging from 250 degrees C to 650 degrees C. Transmission electron microscopy (TEM) and Atom probe tomography (APT) were employed to study the evolution of structural damage and phase stability with irradiation temperature. Al0.3CoCrFeNi exhibited a similar evolution of irradiation-induced defects with temperature as compared with conventional FCC alloys. At 250 degrees C and 350 degrees C, most of the visible irradiation-induced defects were faulted 1/3(111) dislocation loops. As the irradiation temperature increased to 500 degrees C, perfect 1/2(110) dislocation loops were observed along with the faulted loops. At the highest irradiation temperature 650 degrees C, only dislocation lines and networks could be observed. Regarding phase stability, the 3 MeV Au irradiation was observed to suppress the precipitation of (Ni, Al)-enriched nano clusters and the L12 ordered structure at irradiation temperatures 250 degrees C to 500 degrees C whereas precipitation of the B2 ordered structure was accelerated at 650 degrees C. This resulted in qualitatively opposite precipitation behavior between the ion irradiated damage region and unirradiated region at 500 degrees C and 650 degrees C. The opposite phase stability of the ion-irradiated damage region and unirradiated region at different temperatures is attributed to the competing effects of ballistic dissolution vs irradiation enhanced diffusion on precipitation. (C) 2020 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Observations of Percolation Structures Induced in Thin Solid Films by Ion Irradiation

Percolation Scale Effects Upon Amorphous Structural Phase-Transition in an Alloy Film

Observations of Fractal Patterns Induced in Thin Solid Films by Ion Irradiation.

Role of Carrier Concentration in Swift Heavy Ion Irradiation Induced Surface Modifications

Some New Structural Transformations Induced By Ion-Beams

Ion-irradiation-induced Structural Evolution in Ti4AlN3

Irradiation-induced structural transitions in Ti 2 AlC

The Structural Transitions of Ti3AlC2 Induced by Ion Irradiation

Comparative Study of Irradiation-induced and Thermally Induced Structural Phase Transitions in Equilibrium Immiscible Fe–Ag Systems

Ion Irradiation Induced Nanocrystal Formation in Amorphous Zr55cu30al10ni5 Alloy

Irradiation-induced Alloying in an Immiscible TaTi System

Irradiation induced non-equilibrium phase formation and structural transformation in the Fe–Ti–Nb multilayered films

Effect of ion irradiation on superconducting thin films

FRACTAL GROWTH OF NICKEL-BASED ALLOYS IN THIN FILMS

Self-ion Irradiation Response of (cocrfeni)94ti2al4 Alloy Containing Coherent Nanoprecipitates

A new mechanism of surface phase formation on precipitation-hardening alloy under ion irradiation

Mechanical Properties and Structure Evolution of Single-Crystalline Silicon Irradiated by 1 MeV Au+ and Cu+ Ions

Structural Phase Transition Induced by Ion Irradiation in the Equilibrium Immiscible Ag–Co System

Structural Damage and Phase Stability of Al0.3CoCrFeNi High Entropy Alloy under High Temperature Ion Irradiation

On the Evidence for Postacceleration Effects in Breakup Reactions with Halo Nuclei

In situ heavy ion irradiation studies of nanopore shrinkage and enhanced radiation tolerance of nanoporous Au