Abstract:Acetylene (C2H2) plasma immersion ion implantation (PIII) into polyurethane (PU) films was performed with different processing times of from 8 to 40 minutes. The surface properties were characterized by means of contact angle measurement, X-ray photoelectron spectroscopy (XPS), and attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR). The contact angle of water decreased from the original 79.2°to 42.5° and the surface energy increased from 41.1 mN/m to 55.8 mN/m. The results show that the water wettability of PU was improved by PIII. The blood compatibility of the modified PU films was studied by platelet adhesion tests. The results showed significant difference for the behavior of platelet adhesion between different PU films. The statistical number of adherent platelets on the surface of PU per 1200 μm2 after 15 min incubation showed that an average of 25 to 28 contact-adherent platelets were present on the untreated PU film. In contrast, the number of platelets adhered on the surface of PU that was treated by acetylene PIII for 8 minutes was less than half of the platelets on the untreated PU film. This suggests that adhesion of platelets is significantly suppressed on the surface of PU modified by C2H 2 PIII. Photographs of scanning electron microscopy (SEM) showed that the adherent platelets on the surface of PU after C2H 2 PIII at suitable treatment process had few aggregations and pseudopodiums. XPS spectra showed that the carbon content on the PU surface was increased after C2H2 implantation. Furthermore, the result of ATR-FTIR indicated that the characteristic adsorption peak at wavenumber 1657 cm-1 corresponding to -C=C- can be found on the PIII-treated PU surface, whereas this characteristic adsorption peak cannot be detected on the untreated surface. This indicates that polyacetylene chains were formed and grafted on PU surface by C2H2 plasma immersion ion implantation. This suggests that the improvement of the platelet adhesion of modified PU might come from the destruction of original surface chemical bonds and formation of polyacetylene chains by PIII.

Surface Modification of Medical Polyurethane by Plasma Treatment

Analysis of Low Temperature Plasma on Polyurethane Surface

Surface Modification of Polycarbonate Urethane by Low-Temperature Ammonia Plasma

Surface Modification of Polycarbonate Urethane by Allylamine Plasma

Surface Modification of Medical Polyurethane by Acetylene Plasma Immersion Ion Implantation

Surface modification of UHMWPE fiber via low-temperature plasma

Different Low-Temperature Plasma Treatments of Polyurethane and the Evaluation of Their Biocompatibility

Surface modification of a biomedical polyethylene terephthalate (PET) by air plasma

Surface Modification of Polytetrafluoroethylene by Microwave Plasma Treatment of H2O/Ar Mixture at Low Pressure

Surface modification of polypropylene non-woven fabric using atmospheric nitrogen dielectric barrier discharge plasma

Studies of Wettability of Medical Pvc by Remote Nitrogen Plasma

Polypropylene Surface Plasma Modification Using Middle Frequency Power Supply

Surface Modification of Medical PVC by Remote Oxygen Plasma

Characterization of Active Screen Plasma Modified Polyurethane Surfaces

THE SURFACE TREATMENT OF POROUS POLYPROPYLENE MEMBRANE BY AR PLASMA WITH A LOW POWER

Maskless Surface Modification of Polyurethane Films by an Atmospheric Pressure He/O₂ Plasma Microjet for Gelatin Immobilization.

Effect of Non‐Thermal Sulfur Hexafluoride Cold Plasma Modification on Surface Properties of Polyoxymethylene

Plasma Treatment of Polymethyl Methacrylate to Improve Surface Hydrophilicity and Antifouling Performance

Studies on Surface Modification of Poly(tetrafluoroethylene) Film by Remote and Direct Ar Plasma

Investigation on the Effects and Mechanisms of Ptfe Surface Modification by Low Pressure Plasma

Controlling Surface Properties of Electrospun Polyphenylsulfone Using Plasma Treatment and X-ray Photoelectron Spectroscopy.