THE SURFACE TREATMENT OF POROUS POLYPROPYLENE MEMBRANE BY AR PLASMA WITH A LOW POWER

Yan Hui,Dong Rugui,Huang Jian,Wang Xiaolin

DOI: https://doi.org/10.3969/j.issn.1000-3770.2013.07.007

2013-01-01

Abstract:The surface treatment of porous polypropylene membrane was carried out by Ar plasma with a low power of 1 W.After the detailed investigation of surface etch effects by the plasma atmosphere pressure and the plasma time based on the weight-loss measurement and SEM observation,the surface modification of pore walls into the porous membrane was evaluated based on the water flux method.More surface etches occurred by plasma treatments with lower atmosphere pressures and longer plasma times,and thorough surface modification on the pore walls of the porous membrane was achieved by plasma treatments with the medium atmosphere pressure of 18 Pa or 30 Pa,when the plasma time was enough(10 min).It is obvious that the active species with enough energy level and specie amount in the plasma atmosphere would be responsible for the thorough surface treatment throughout the membrane pores.In the end,an optimal plasma condition with the atmosphere pressure at 18 Pa and the plasma time of 10 min was determined,when only a slight surface etch was induced.A hydrophilic surface with a contact angle of 44.2°has been reached when some polar carboxyl groups was produced on the surface by plasma treatment.However,the surface contact angle would increase sharply to 66.0°in 5 d,subsequently become relatively steady in 1 a.