Abstract:Ultrahigh molecular weight polyethylene (UHMWPE) is an excellent material with high performance, but it is very difficult to covalently introduce functional groups on its surface owing to its inherently inert structure, which constrains its further application. In this study, vinyl triethoxysilane (VTEOS) containing hydrolysable alkoxyl groups was in situ grafted on UHMWPE by air plasma treatment. The plasma treatment conditions for VTEOS grafting were optimized. The structure of the modified UHMWPE was characterized with FTIR and XPS. The relatively high VTEOS content was obtained when the treating conditions were about 20 W, 125 Pa for 10 min. And FTIR results showed that the grafted structure on the surface was stable for long time duration in the ambient environment. After the treatment, the roughness of the surface increased and the water contact angle of the modified sample dropped to 47.5 degrees from 92.8 degrees of the unmodified one. TGA and XRD results indicated that plasma treatment would not change the bulk structure of UHMWPE greatly. Cell culture experiments showed that fibroblasts on the modified samples had notably high viability and proliferation rate with good adhesion shape. Hence, it might be an effective method to improve the surface properties of UHMWPE for biomedical applications by plasma-induced in-situ grafting with VTEOS. (c) 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 106A: 321-332, 2018.

Surface modification of UHMWPE fiber via low-temperature plasma

Effects of Surface Modification by Argon Plasma on Peel Strength of Woven-Type Ultrahigh-Molecular-Weight Polyethylene

Surface modification of ultrahigh molecular weight polyethylene by plasma-induced in-situ grafting with vinyl triethoxysilane.

Surface modification of ethylene propylene diene monomer by low temperature plasma

Studies on the Surface Modification of High Performance Organic Fibers by the Plasma Technology

Low Density Polyethylene(Ldpe) Surface Modification and Its Adhesion after Low Temperature Plasma Treatment

Surface Modification of Medical Polyurethane by Plasma Treatment

Effects of Argon Plasma Treatment on the Adhesion Property of Ultra High Molecular Weight Polyethylene (UHMWPE) Textile

Polypropylene Surface Plasma Modification Using Middle Frequency Power Supply

Surface Modification of Polytetrafluoroethylene by Microwave Plasma Treatment of H2O/Ar Mixture at Low Pressure

A low power 50 Hz argon plasma for surface modification of polytetrafluoroethylene

Interfacial performance and impact resistance of argon plasma treated UHMWPE/STF inter-ply hybrid composites

Surface modification of a biomedical polyethylene terephthalate (PET) by air plasma

THE SURFACE TREATMENT OF POROUS POLYPROPYLENE MEMBRANE BY AR PLASMA WITH A LOW POWER

Dielectric barrier discharge plasma treatment of ultrahigh molecular weight polyethylene in different discharge atmospheres at medium pressure: A cell-biomaterial interface study

X-ray Photoelectron Spectroscopic Analysis of Surface Modification of Aramid Fiber by Low Temperature Plasma

Study on the Generation and Modification of Surface Atmospheric Pressure Air Diffuse Discharge Plasma on Aramid Fabric

Structure Modification and Enhancement of Wear Resistance of Ultra-High-Molecular-Weight Polyethylene by Low-Pressure Helium Plasma Treatment

Research On Surface Modification Of Polytetrafluoroethylene Coupled With Argon Dielectric Barrier Discharge Plasma Jet Characteristics

Surface Modification of High-Strength Polyethylene Fiber by Plasma Treatment

Synergetic enhancement of interfacial properties and impact resistant of UHMWPE fiber reinforced composites by oxygen plasma modification