Different Low-Temperature Plasma Treatments of Polyurethane and the Evaluation of Their Biocompatibility

ZHANG Yan-bo,JIANG Ming,HU Ping,WU Qing-yu,WANG Qiang,WANG Xu

2011-01-01

Abstract:Objective To provide scaffold material with good tissue compatibility for constructing tissue engineering blood vessel.Methods Low-temperature plasma of CO2,O2,NH3 and SO2 were used for 2,5,10 and 15 minutes respectively to treat the surface of polyurethane.The changes of physical and chemical characteristics and tissue compatibility of the polyurethane's surface were evaluated and compared by biologic and material methods.Results Polyurethane membranes treated with CO2,O2,and NH3 plasma had the same appearance with the untreated polyurethane.Inverted phase contrast microscope,scanning electron microscope and toluidine blue staining test showed cells grew better after CO2,O2,NH3 plasma irradiation than those before treatment,and cells on the membrane irradiated by O2 for 10 minutes grew better than those irradiated by other plasmas for other irradiation periods.MTT assay showed O2 irradiation for 10 minutes had a higher optical density value compared with the other plasma treated membranes and the untreated membrane(P0.05).After treatment,the surface roughness increased and some polar groups such as-OH,-COOH,-NH2 and-SO3H were successfully introduced to the surface,which significantly improved tissue compatibility of polyurethane's surface.The improved compatibility of polyurethane treated by O2 plasma for 10 minutes was the best.Conclusion Low-temperature plasma is an effective method to improve the tissue compatibility of polyurethane and O2 irradiation for 10 minutes is the optimum treating condition.