Surface Modification of Polycarbonate Urethane by Low-Temperature Ammonia Plasma

Yakai Feng,Wenli Guan,Haiyang Zhao,Jintang Guo,Qingliang Chen,Jianshi Liu

DOI: https://doi.org/10.16865/j.cnki.1000-7555.2011.05.014

2011-01-01

Abstract:The polycarbonateurethane(PU) surface was modified by low-temperature ammonia plasma.The influences of modification conditions on the contact angle,amine content and surface morphology were investigated by water contact angle,scanning electron microscope(SEM) and X-ray photoelectron specroscopy(XPS).The results show that the hydrophilicity of PU surface is improved significantly after ammonia plasma modification.The water contact angle decreases with amine content on the surface increasing.The smooth surface gradually becomes rough after plasma modification.The surface morphology is different with different modified conditions.The C/N ratio on the surface increases from 2.44% to 3.98% after treatment,respectively.Water contact angle increases quickly in 5 h and then does not change any more within 10 h after plasma modification.As expected the ammonia plasma modified PU has good biocompatibility for preferred candidates for vascular graft.