Abstract:A new type of poly-diamond plate without a catalyst was produced via the high-pressure high-temperature (HPHT) compression of diamond powders. The densification of diamond powders and sp3 to sp2 carbon on the surface under HPHT compression was investigated through the characterization of the microstructure, Raman spectroscopy analysis and electrical resistance measurement. The densification and sp3-sp2 transformation on the surface are mainly affected by the pressure, temperature and particle size. The quantitative analysis of the diamond sp3 and sp2 carbon amount was performed through the peak fitting of Raman spectra. It was found that finer diamond particles under a higher temperature and a lower pressure tend to produce more sp2 carbon; otherwise, they produce less. In addition, it is interesting to note that the local residual stresses measured using Raman spectra increase with the diamond particle size. The suspected reason is that the increased particle size reduces the number of contact points, resulting in a higher localized pressure at each contact point. The hypothesis was supported by finite element calculation. This study provides detailed and quantitative data about the densification of diamond powders and sp3 to sp2 transformation on the surface under HPHT treatment, which is valuable for the sintering of polycrystalline diamonds (PCDs) and the HPHT treatment of diamonds.

Spark Plasma Sintering Assisted Diamond Formation From Carbon Nanotubes At Very Low Pressure

Conversion of carbon nanotubes to diamond by spark plasma sintering

Pulsed Electric Field Induced Diamond Synthesis from Carbon Nanotubes with Solvent Catalysts

Diamond Synthesis Through the Generation of Plasma During Spark Plasma Sintering

Nano-polycrystalline diamond formation under ultra-high pressure

Synthesis of Nano-Polycrystalline Diamond under High Pressure and High Temperature

Diamond synthesis from carbon nanofibers at low temperature and low pressure

Growth of Diamond from Fullerene C60 by Spark Plasma Sintering

Thermal Stability of Carbon Nanotubes, Fullerene and Graphite under Spark Plasma Sintering

Phase Change of Nano Carbon Materials and Diamond Synthesis Under Effect of DC Pulsed Electric Field

Plasma-Induced Transformation of Carbon Nanotubes to Nanocrystalline Diamond

Synthesis and Mechanism Study of Carbon Nanowires, Carbon Nanotubes, and Carbon Pompons on Single-Crystal Diamonds

Pressure Effects on Nanotubes Formation Using the Submerged Arc in Water Method

Preparation of Multi-Walled Carbon Nanotube-Reinforced TiNi Matrix Composites from Elemental Powders by Spark Plasma Sintering

Synthesis and Characterization of Diamond Nanowires from Carbon Nanotubes

Dispersion and Structural Evolution of Multi-Walled Carbon Nanotubes in ZrB2 Matrix

Densification and Surface Carbon Transformation of Diamond Powders under High Pressure and High Temperature

Characterization and Formation Mechanism of the Nanodiamond Synthesized by A High Energy Arc‐Plasma

Pulsed Direct Current Field-Induced Thermal Stability And Phase Transformation Of Nanodiamonds To Carbon Onions

Shear driven formation of nano-diamonds at sub-gigapascals and 300 K

Rapid and Low Temperature Spark Plasma Sintering Synthesis of Novel Carbon Nanotube Reinforced Titanium Matrix Composites