Abstract:Due to the great impact of hydrogen on the thermodynamics, and chemically facilitates phase transition, self‐catalyzed hydrogenated carbon nano‐onions (HCNOs) make the synthesis of transparent nano‐polycrystalline diamond (t‐NPD) under low pressure and temperature conditions, 10 GPa, 1600 °C and 15 GPa, 1350 °C. Facile and industrial‐scale synthesis of HCNOs precursor, and mild synthesis conditions give t‐NPD a wide potential application. Transparent nano‐polycrystalline diamond (t‐NPD) possesses superior mechanical properties compared to single and traditional polycrystalline diamonds. However, the harsh synthetic conditions significantly limit its synthesis and applications. In this study, a synthesis routine is presented for t‐NPD under low pressure and low temperature conditions, 10 GPa, 1600 °C and 15 GPa, 1350 °C similar with the synthesis condition of organic precursor. Self‐catalyzed hydrogenated carbon nano‐onions (HCNOs) from the combustion of naphthalene enable synthesis under nearly industrial conditions, which are like organic precursor and much lower than that of graphite and other carbon allotropes. This is made possible thanks to the significant impact of hydrogen on the thermodynamics, as it chemically facilitates phase transition. Ubiquitous nanotwinned structures are observed throughout t‐NPD due to the high concentration of puckered layers and stacking faults of HCNOs, which impart a Vickers hardness about 140 GPa. This high hardness and optical transparency can be attributed to the nanocrystalline grain size, thin intergranular films, absence of secondary phase and pore‐free features. The facile and industrial‐scale synthesis of the HCNOs precursor, and mild synthesis conditions make t‐NPD suitable for a wide range of potential applications.

Catalyst-Free Synthesis Of Transparent, Mesoporous Diamond Monoliths From Periodic Mesoporous Carbon Cmk-8

Synthesis of Nanopolycrystalline Mesoporous Diamond from Periodic Mesoporous Carbon: Mesoporosity Increases with Increasing Synthesis Pressure

Synthesis of Nano-Polycrystalline Diamond under High Pressure and High Temperature

Nano-polycrystalline diamond formation under ultra-high pressure

Facile Diamond Synthesis from Lower Diamondoids

Metastable Carbon at Extreme Conditions

Size tunable synthesis of solution processable diamond nanocrystals.

Synthesis of quenchable amorphous diamond

On the High-Pressure Behavior of Periodic Mesoscale SBA-16 Silica/carbon Composites: Studies at 10 GPa Between 25 and 1800 °C

Shear driven formation of nano-diamonds at sub-gigapascals and 300 K

Smooth Thin-Film C/Diamond Membranes With Controllable Optical Band-Gaps

Synthesis and Mechanism Study of Carbon Nanowires, Carbon Nanotubes, and Carbon Pompons on Single-Crystal Diamonds

Narrow-gap, Semiconducting, Superhard Amorphous Carbon with High Toughness, Derived from C60 Fullerene

Self‐Catalyzed Hydrogenated Carbon Nano‐Onions Facilitates Mild Synthesis of Transparent Nano‐Polycrystalline Diamond

Ultrastrong catalyst-free polycrystalline diamond

Rare-earth metal catalysts for high-pressure synthesis of rare diamonds

Heat-treated Glassy Carbon under Pressure Exhibiting Superior Hardness, Strength and Elasticity

Amorphous Diamond: A High-Pressure Superhard Carbon Allotrope

Transparent diamond ceramics from diamond powder

High Pressure High Temperature Synthesis of Highly Boron Doped Diamond Microparticles and Porous Electrodes for Electrochemical Applications

Diamond with Unexpected Multi‐Scale Pores