Abstract:A new woodceramics was developed by carbonizing phenolic resin–basswood powder composite under vacuum. Structural characterization of woodceramics was performed by scanning electron microscopy (SEM), X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR) techniques. The pyrolytic behaviors of basswood powder and phenolic resin were studied by thermogravimetric analysis (TGA). The effects of carbonization temperature and weight ratio of phenolic resin to basswood powder on the volume electrical resistivity, open porosity and bending strength of woodceramics were also investigated. Experimental results show that woodceramics has a topologically uniform interconnected porous network microstructure, and is typical non-graphitizable carbon containing CC bonds, COC bonds and CH structure. With increasing carbonization temperature, the (002) peak becomes stronger, the (002) interplanar spacing and volume electrical resistivity decrease, and the dimensions of carbonized wood powder decrease, while the space between carbonized basswood powders and the open porosity and bending strength of woodceramics increase. The increasing weight ratio of phenolic resin to basswood powder improves the forming ability of phenolic resin impregnated wood powders, and results in a more uniform microstructure, but there is a slight effect on the XRD pattern of woodceramics. The volume electrical resistivity and open porosity decrease, and the bending strength increases as the weight ratio of phenolic resin to wood powder increases.

Effect of carbonization temperature on the basic properties of woodceramics impregnated with liquefied wood

Effect of carbonization temperature on the basic properties of woodceramics made from carbonized bamboo fiber and liquefied wood

Effect of carbonizing speed on the property changes of woodceramics impregnated with liquefacient wood

Effect of carbonization temperature on the structural changes of woodceramics impregnated with liquefied wood

Effect of Components upon the Surface Area of Woodceramics

Woodceramics Prepared from Wood Powder/Phenolated Wood Composite

Research on Fire Retardant Performance of Wood with the Compound of Potassium Carbonate and SiO2 Gels

STUDY ON STRUCTURAL CHANGES DURING PREPARING WOODCERAMICS FROM PHENOLIC RESIN/BASSWOOD POWDER COMPOSITE

Effect of Phenolic Resin on the Basic Properties of Woodceramics and Biomorphic SiC Ceramics

Structure and basic properties of woodceramics made from phenolic resin–basswood powder composite

Effects of Carbonization Temperature and Component Ratio on Electromagnetic Interference Shielding Effectiveness of Woodceramics.

Woodceramics Prepared from Basswood Powder and Phenolic Resin

Study on Woodceramics Compressed by Hydrothermal

Effect of processing methods and condition of raw materials on the impregnation of phenolic resinand the shape of Woodceramics after burning

Surface Area Characteristics of Woodceramics

Morphology and damping characteristics of woodceramics

Experimental Study on Elastic Modulus and Damping Capacity of Woodceramics

WOODCERAMICS COMPOSITES WITH INTERPENETRATING NETWORK

Study on Carbonization Mechanism of Common Paper Template Cellulose and Preparation of Porous Wooden Ceramic

Porous SiC Ceramic Prepared by Reactive Infiltration of Liquid Silicon into Woodceramics

The preparation of CaCO3/wood composites using a chemical precipitation method and its flame-retardant and mechanically beneficial properties