Abstract:A new woodceramics was developed by carbonizing phenolic resin–basswood powder composite under vacuum. Structural characterization of woodceramics was performed by scanning electron microscopy (SEM), X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR) techniques. The pyrolytic behaviors of basswood powder and phenolic resin were studied by thermogravimetric analysis (TGA). The effects of carbonization temperature and weight ratio of phenolic resin to basswood powder on the volume electrical resistivity, open porosity and bending strength of woodceramics were also investigated. Experimental results show that woodceramics has a topologically uniform interconnected porous network microstructure, and is typical non-graphitizable carbon containing CC bonds, COC bonds and CH structure. With increasing carbonization temperature, the (002) peak becomes stronger, the (002) interplanar spacing and volume electrical resistivity decrease, and the dimensions of carbonized wood powder decrease, while the space between carbonized basswood powders and the open porosity and bending strength of woodceramics increase. The increasing weight ratio of phenolic resin to basswood powder improves the forming ability of phenolic resin impregnated wood powders, and results in a more uniform microstructure, but there is a slight effect on the XRD pattern of woodceramics. The volume electrical resistivity and open porosity decrease, and the bending strength increases as the weight ratio of phenolic resin to wood powder increases.

Study on Woodceramics Compressed by Hydrothermal

Experimental Studies on Chopping Cotton Stalk when Compressed to High Densities

WOODCERAMICS COMPOSITES WITH INTERPENETRATING NETWORK

Effects of High-Pressure Treatment on Poplar Wood: Density Profile, Mechanical Properties, Strength Potential Index, and Microstructure

STUDY ON STRUCTURAL CHANGES DURING PREPARING WOODCERAMICS FROM PHENOLIC RESIN/BASSWOOD POWDER COMPOSITE

FABRICATION AND PROPERTIES OF HIGH DAMPING WOODCERAMICS/MB15 COMPOSITE

High-Pressure Treatment of Chinese Fir Wood: Effect on Density, Mechanical Properties, Humidity-Related Moisture Migration, and Dimensional Stability

Experimental Study on Elastic Modulus and Damping Capacity of Woodceramics

Increasing the Mechanical Properties of High Damping Woodceramics by Infiltration with a Magnesium Alloy

Effect of High-pressure Densification on Moisture Sorption Properties of Paulownia Wood

Porous SiC Ceramic Prepared by Reactive Infiltration of Liquid Silicon into Woodceramics

Study on preparation and properties of wood-ceramics

Woodceramics Prepared from Basswood Powder and Phenolic Resin

Morphology and damping characteristics of woodceramics

Effect of carbonization temperature on the basic properties of woodceramics made from carbonized bamboo fiber and liquefied wood

Effect of carbonization temperature on the basic properties of woodceramics impregnated with liquefied wood

Structure and basic properties of woodceramics made from phenolic resin–basswood powder composite

Effect of carbonization temperature on the structural changes of woodceramics impregnated with liquefied wood

The fabrication of composites with interpenetrating networks based on woodceramics

Progress and Application Prospects of Woodceramics

Effect of carbonizing speed on the property changes of woodceramics impregnated with liquefacient wood