Abstract:TiSiN-Ag nanocomposite coatings with different Ag contents were deposited on Ti-6Al-4V using reactive co-sputtering in multi-arc ion plating system. Influence of Ag contents on structure and tribological properties of TiSiN-Ag nanocomposite coatings was investigated. The TiSiN-Ag coatings were found to have unique nanocomposite structures composed of nanocrystallite and amorphous nc-TiN/nc-Ag/a-Si3N4. When the silver content was 1.4 at.%, the coating exhibited high hardness (36 GPa), but poor wear resistance. When the silver content was increased from 5.3 to 8.7 at.%, the coatings possessed homogeneous distribution and small variation in hardness. Although these coatings revealed obvious decrease in hardness, significantly reduced in the friction coefficient and possessed excellent tribological properties, besides, the coating with the Ag content of 5.3 at.% showed best wear resistance in artificial seawater and the coating (7.9 at.% Ag) revealed the best wear resistance in ambient air. However, with a further increased incorporation of Ag into the TiSiN-Ag coating (17.0 at.%) resulted in the formation of a large volume fraction of metallic silver, which caused a decrease both in hardness and wear resistance. The coating containing highest Ag concentration (21.0 at.%) exhibited low friction coefficient both in ambient air and artificial seawater, although possessing low hardness. (C) 2016 Elsevier B.V. All rights reserved.

Friction and Wear Properties of Sputtered WS2/Ag Nanocomposite Films in Different Environments

Microstructure and Tribological Behavior of WS2–Ag Composite Films Deposited by RF Magnetron Sputtering

Microstructure and Tribological Behavior of the WS_2-Ag Composite Films Deposited by Radio Frequency Magnetron Sputtering in Different Environments

Effect of Ag Content on Microstructure and Tribological Performance of WS2–Ag Composite Films

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Effect of Lubricating Condition on Tribological Properties of Nano-SiO2 Filled Polyamide Composite

FRICTION AND WEAR PROPERTIES OF NANOCOMPOSITE COATINGS INCLUDING INORGANIC FULLERENE-LIKE (mo, W)S2 IN ENVIRONMENTS

Microstructure and Tribological Properties of Co-sputtered MoS2/WS2 Composite Films

Tribological Properties of WS2 Composite Film Prepared by a Two-Step Method

Influence of Ag Contents on Structure and Tribological Properties of TiSiN-Ag Nanocomposite Coatings on Ti–6Al–4V

Frictional Behavior and Wear Mechanisms of Ag/MoS 2 /WS 2 Composite Under Reciprocating Microscale Sliding

Tribological behavior and microstructural evolution of lubricating film of silver matrix self-lubricating nanocomposite

Microstructure and tribological behaviors of magnetron sputtered WS2/Fe/a-C/Fe multilayer films with various deposition temperatures

Microstructure, Chemical and Tribological Investigations of Mo X W1−x S Y Co-Sputtered Composite Films

Microstructure, chemical and tribological investigations of Mo<sub><i>x</i></sub>W<sub>1−<i>x</i></sub>S<sub><i>y</i></sub> co-sputtered composite films

Friction and wear properties of CrSiCN coatings with low carbon content as sliding against SiC and steel balls in water

Influence of C Dopant on the Structure, Mechanical and Tribological Properties of R.F.-Sputtered Mos2/A-C Composite Films

Wear performance of the plasma sprayed fine WC-Co composite powders coatings

Tribological properties of magnetron sputtered MoS2/metal (Ti, Mo) nanocomposite coatings

Friction maps and wear maps of Ag/MoS2/WS2 nanocomposite with different sliding speed and normal force

Preparation and tribological behavior of TiN/a-C composite films deposited by DC magnetron sputtering