Influence of Carbon Coat by Chemical Vapor Deposition on Tensile Behavior and Fracture Characteristics of SiC Filament

LIU Cui-xia,YANG Yan-qing,LUO Xian

DOI: https://doi.org/10.3969/j.issn.1673-9965.2012.12.011

2012-01-01

Abstract:In order to resolve low strength fracture of SiC filament caused by its surface defect,the SiC filament is coated by carbon with chemical vapor deposition method.For carbon coat and non-carbon coat SiC filament,their crystal structure and surface morphology are to be characterized with X-ray diffraction and SEM respectively.Their tensile strength is tested.The result shows that SiC filament is composed of β-SiC,whose(111) direction is the preferred orientation.The surface of carbon coat SiC filament is smooth and dense with less surface defect.The depth value of surface defects is effectively reduced.Compared to the strength of SiC filament without carbon coat,strength of SiC filament with carbon coat is increased for nearly one-third.Therefore,the carbon coat reduces surface defect,which increases the tensile strength of SiC filament greatly.