Stable, Easily Sintered BaCe0.5Zr0.3Y0.16Zn0.04O3−δ Electrolyte-Based Proton-Conducting Solid Oxide Fuel Cells by Gel-Casting and Suspension Spray
Bin Lin,Yingchao Dong,Songlin Wang,Daru Fang,Hanping Ding,Xiaozhen Zhang,Xingqin Liu,Guangyao Meng
DOI: https://doi.org/10.1016/j.jallcom.2008.11.154
IF: 6.2
2009-01-01
Journal of Alloys and Compounds
Abstract:Protonic ceramic membrane fuel cells (PCMFCs) based on oxide proton conductors exhibit more advantages than traditional solid oxide fuel cells (SOFCs) based on oxygen-ion conducting electrolytes, such as low activation energy and high energy efficiency. In order to develop a simple and cost-effective route to fabricate PCMFCs with SrCo 0.9 Sb 0.1 O 3− δ (SCS) cubic perovskite cathode, a dense BaCe 0.5 Zr 0.3 Y 0.16 Zn 0.04 O 3− δ (BCZYZn) electrolyte was fabricated in situ metal oxide on a porous anode support by gel-casting and suspension spray, which is cost-effective, easy to realize, and suitable for mass-production. The key part of this process is to directly spray well-mixed suspension of BaCO 3 , CeO 2 , ZrO 2 , Y 2 O 3 and ZnO instead of pre-synthesized BCZYZn ceramic powder on the anode substrate. With SCS cubic perovskite cathode synthesized by gel-casting on the bi-layer, single cells were assembled and tested with H 2 as fuel and the static air as oxidant. An open-circuit potential of 0.987 V, a maximum power density of 364 mW cm −2 , and a low polarization resistance of the electrodes of 0.07 Ω cm 2 was achieved at 700 °C.