Abstract:During the bearing service, a series of microstructural evolutions will arise inside the material, such as the appearance of feature microstructures. The essential reason for the microstructural evolution is the cumulative effect of cyclic stress. The Hertz Contact formula is usually adopted to calculate the internal stress, and there is a correlation between the shape and distribution of the feature microstructure and the stress distribution. But it is insufficient to explain the relationship between the morphology of feature microstructures and the rolling direction, such as specific angles in butterfly and white etching bands. The rolling phenomenon will cause the asymmetry of stress distribution in the material, which is the source of the rolling friction coefficient. Moreover, slipping or microslip will produce additional stress components, which also cause the asymmetry of the stress field. However, there is no experimental or theoretical explanation for the relationship between the asymmetry of the stress field and the feature microstructure. According to the current theory, the appearance of feature microstructures is caused by stress with or without rolling. Therefore, it is of great significance to study the formation mechanism: whether feature microstructures will appear in the uniaxial cyclic compression stress field without rolling. In this paper, uniaxial cyclic compressive stress was loaded into a plate-ball system and a cylinder system. The characteristics of microstructural change of bearing steel (GCr15) were studied. It was found that the hardness of the material increased after the cyclic compressive load, and the inclusions interacted with the matrix material. In the local microregion a white etching area was found, although the scale is very small. No large-scale feature microstructures appeared. Other phenomena in the experiment are also described and analyzed. For example, the production of oil film in the contact area and the changing law of alternating load.

Fracture Analysis of GCr15 Steel Cycloid Gear

Fracture Analysis on Gear Shaft in Vulcanizer Tire Foundation

X-ray diffraction comparison studies between the laser hardened gear and carburized gear

Fracture failure analysis of the teeth of conjunction gear made of 20MnCr5S steel

Fracture failure analysis on Alloy783 bolts in medium-pressure valve bonnets of USC units

Failure analysis for outer ring cracking of GCr15 rolling bearing

Analysis on surface spalling failure of 20CrMnTi steel gear

Fracture Analysis of High Chromium Cast Iron Roll on CSP Mill

Fracture failure analysis of transmission gear shaft in a bidirectional gear pump

Modeling and Analysis of Deformation for Spiral Bevel Gear in Die Quenching Based on the Hardenability Variation

Fracture analysis on involute spline of large tunnel boring machine

Preliminary Research on Response of GCr15 Bearing Steel under Cyclic Compression

FAILURE ANALYSIS ON MAIN GEAR FOR BM50 GRINDING MACHINE

Failure analysis on the plumbing arm of automobile steering gear

Surface Morphology and Subsurface Microstructure Evolution when Form Grinding 20cr2ni4a Alloys.

Sliding Friction and Wear Properties of GCr15 Steel under Different Lubrication Conditions

Atomic-Scale Insights into Damage Mechanisms of GGr15 Bearing Steel Under Cyclic Shear Fatigue

Failure analysis of the carburized 20MnCr5 gear in fatigue working condition

Analysis on wear patterns and mechanisms of carbide tool for face-hobbing of spiral bevel gear

Experimental Study on the Influence of Surface Carbon Content on Crack Initiation for 20Cr2Ni4A Steel

Failure Analysis of Fatigue Fracture on the Outer Ring of a Cylindrical Roller Bearing in an Air Blower Motor