Effects of Rare Earth on Microstructure and Corrosion Resistance of Hot–dip Aluminum Coating

SUN Wei,CAI Qi-zhou,LUO Qiang
DOI: https://doi.org/10.3969/j.issn.1007-9289.2010.06.005
2010-01-01
China surface engineering
Abstract:The effects of rare earth on microstructure and corrosion resistance of hot-dip aluminum coating were studied.The results show that a two-layer coating is formed,consisted of an external Al layer with Al and FeAl3 as well as an interlayer with Fe2Al5 and FeAl3,interlayer and the substrate take the shape of jagged metallurgical bonding.The Al layer becomes thinner with increasing the rare earth content from 0.0 %~0.5 %,then it gets thicker when the RE content exceeds 0.5 %.But the thickness of interlayer begins obviously increased when the content of 0.1 % RE is added,then it gets thinner gradually when the content of RE is more than 0.1 %.It is also found that FeAl3 phase formed in hot-dip aluminum coating is refined by RE in this paper.Potentiodynamic polarization measurements and salt water(5 % NaCl) corrosion test reveal that hot-dip aluminum coating with 0.5 % RE possesses the best corrosion resistance,which is 4 times as much as that of 45 steel,2 times as much as that of without RE respectively.
What problem does this paper attempt to address?