Abstract:Aiming at enhancing the electrochemical characteristic of RE-Mg-based composite, the partial substituting La with Ce experiment in the composites was conducted, and the surface modification treatment of the alloys was performed by mechanical coating Ni. By means of mechanical trituration, The La 10-x Ce x Mg 80 Ni 5 (x = 0–2) + y wt% Ni (y = 50–200) compound materials which have the structures of nanocrystalline and amorphous were synthesized. In order to make sense of the principle action of Ce and Ni elements in structural and electrochemical properties of the material, some deep research were carried out. According to the final results, the as-milled composites have the electrochemical hydrogen absorption and hydrogen desorption abilities at room temperature. Having no use for activation, the as-milled composites can reach the maximum discharge capacities when the first cycling was carried out. With the Ni value x changed from 50 to 200, the discharge capacity was varied from 70.5 mAh/g to 902.1 mAh/g; moreover, the capacity retention rate at 20th cycle (S 20 ) and high rate dischargeability (HRD) of the (x = 0) composite were heightened from 67.2 % to 82.3 %, from 50.6 % to 55.7 % respectively. The composites' (y = 100) discharge capacity has a maximum value 118.5 mAh/g when the Ce value x is 1. The capacity retention rate (S 20 ) is enhanced from 53.3 % to 68.5 % by lifting Ce content from x = 0 to x = 2. what's more, the high-rate discharge ability (HRD), the electrochemical impedance spectrum (EIS), potentiodynamic polarization curves, and potential-step measurements all intimate that substituting La with Ce clearly promotes the composites' electrochemical kinetic properties, but maximum values emerge only when the x value is 1.

Effect of Rare Earth Element Ce and La on Corrosion Behavior of AM60 Magnesium Alloy

Influence of Rare Earth Element Ce and La Addition on Corrosion Behavior of Az91 Magnesium Alloy

Corrosion Behaviour of AM60 Magnesium Alloys Containing Ce or La under Thin Electrolyte Layers. Part 2: Corrosion Product and Characterization

Corrosion Behaviour of AM60 Magnesium Alloys Containing Ce or La under Thin Electrolyte Layers. Part 1: Microstructural Characterization and Electrochemical Behaviour

EFFECT OF CERIUM AND LANTHANUM ALLOYING ON MICROSTRUCTURE AND CORROSION BEHAVIOR OF AZ91 MAGNESIUM ALLOY

Influence of mixed rare earth elements(Y and Ce) on the microstructure and corrosion behaviour of Mg-4Al-3Ca alloy

The Effect of Rare Earth on Structures Heredity and Performance of AM60B Magnesium Alloys

Microstructures, tensile properties and corrosion behavior of die-cast Mg–4Al-based alloys containing La and/or Ce

Effect of RE on Microstructure and Properties of AM60 Magnesium Alloy

The Effect of Rare Earths Additions on the Microstructure and the Corrosion Behavior of Sn-0.7Cu-0.075Al Solder Alloy.

EFFECT OF TRACE CE ON THE MICROSTRUCTURE AND CORROSION RESISTANCE OF AZ91 MAGNESIUM ALLOY

Effects of Variable La/Ce Ratio on Microstructure and Mechanical Properties of Mg-5al-0.3mn-1re Alloys

Effect of adding Y and Ce on corrosion behaviour of the extruded ZK60 magnesium alloy

The effect of Ca and rare earth elements on the microstructure, mechanical properties and corrosion behavior of AZ91D

Effects of Rare Earths and Strontium Composite Additions on Microstructure and Properties of AM60 Magnesium Alloy

Effect of Ce replacing La on the electrochemical performance of amorphous grain boundaries Mg-Ni-based materials

Magnesium Alloy Corrosion under Thin Electrolyte Layer Using Electrochemical Impedance Spectroscopy and Polarization Curve

Effects of Rare Earth Elements on Microstructure and Corrosion Resistance of Low Alloy Steel Based on Ultra-Thin Cast Strip Process

A Comparison Study of Ce/La and Ca Microalloying on the Bio-Corrosion Behaviors of Extruded Mg-Zn Alloys

Effect of Cerium on Microstructure, Mechanical Properties and Corrosion Properties of Al-Zn-Mg Alloy

Effect of rare earth elements on the microstructure and property for magnesium alloy AM60B