Interaction and Magnetic Properties of NdCeFeB Melt-Spun Ribbons
Li Minmin,Zuo Jianhua,Hou Yongjie,Bo Yu,Zhang Ming,Dong Fuhai,Li Zhi,Liu Fei,Liu Yanli,Bai Suo,Li Zhubai,Li Yongfeng
2023-01-01
Rare Metal Materials and Engineering
Abstract:The alloy ingots with nominal compositions of (Nd1-xCe2.4Fe14B (x=0, 0.2, 0.4, 0.6, 0.8, 1.0) were prepared by induction melting and then melt-spun to form nanocrystalline ribbons. Phase composition, magnetic properties and microstructure were investigated. XRD results show that all melt-spun ribbons exhibit the tetragonal structure (Nd,Ce)(2)Fe14B phase. When Ce substitution content is more than x=0.6, CeFe2 phase appears and CeFe2 content increases with the increase in Ce substitution content. Remanence, remanence ratio (M-r/M-s) and lattice constant decrease while increasing Ce substitution content. A coercivity of 1.31x10(6) A/m and the maximum energy product of 10(3) kJ/m(3) for (Nd0.8Ce0.2)(2.4)Fe14B melt-spun ribbon are achieved. The coercivity mechanism and intergrain exchange coupling were studied. The positive delta M value was observed in every sample, confirming the existence of exchange coupling interaction. The delta M maximum value reaches 0.76 at the Ce substitution content x=0.2, indicating that the intergranular exchange coupling effect is the strongest, which is consistent with the varying remanence ratio. SEM observation reveals that increasing Ce substitution deteriorates the columnar crystal structure of ribbons.